Polymer Property : Tensile Strength, Yield = 13.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 13.8 MPa
2000 psi
Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable JA306BA Polyvinyl Chloride, Flexible (PVC, Flexible)
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield 13.8 MPa
2000 psi
Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable JG513G2 Polyvinyl Chloride, Flexible (PVC, Flexible)
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield 13.8 MPa
2000 psi
Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable JKC30A Polyvinyl Chloride, Flexible (PVC, Flexible)
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield 13.8 MPa
2000 psi
TM R050-36
Resinlab® EP965LVLX Black Unfilled Electronic Grade Epoxy Encapsulant
Resinlab™ EP965LVLX Black is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has ..
Tensile Strength, Yield 13.8 MPa
2000 psi
Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable W3400L Polyvinyl Chloride, Flexible (PVC, Flexible)
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D1457
Greene Tweed Avalon® 89 PTFE
Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
Techmer ES HiFill® TPU 1000
Availability: North AmericaForms: PelletsFeatures: High DensityAppearance: BlackInformation provided by TP Composites, Inc.
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
Borealis Borstar® HE6067 Black Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables
Borstar HE6067 is a black, bimodal, co-polymer high density polyethylene (HDPE) compound produced according to the bimodal Borstar process. It is characterized by its balanced properties important ..
Tensile Strength, Yield 13.8 MPa
2000 psi
machine direction; ASTM D882
A. Schulman CP80-01 Linear Low-Density Polyethylene
DescriptionCP 880-01 natural is a linear low-density polyethylene having good tensile, stiffness, and toughness properties.ApplicationCP 880-01 meets FDA Regulation 21 CFR 177.1250(c) 3.1 and 3.2.In..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer
DescriptionPolytrope TPP 608 is an olefinic elastomer exhibiting low thermal expansion, low heat sag and high DOI on painted parts. ApplicationTPP 608 is designed specifically for automotive fascia..
Tensile Strength, Yield 13.8 MPa
2000 psi
at 300%; ASTM D412
Lubrizol Estane® MVT 90AF3 Thermoplastic Polyurethane, Moisture Vapor Transmission
Type: Estane® MVT 90AF3 TPU is a 90A aromatic polyether-based thermoplastic polyurethane.Features: High moisture vapor transmission, good physical properties and elasticity, free of organo-tin comp..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
A. Schulman POLYTROPE™ TPP 615 Olefinic Elastomer
DescriptionPolytrope TPP 615 is an olefinic elastomer developed to exhibit very low thermal expansion, high DOI on painted parts with good low temperature impact properties. ApplicationTPP 615 is de..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
A. Schulman POLYTROPE™ TPP 615 Olefinic Elastomer
DescriptionPolytrope TPP 615 is an olefinic elastomer developed to exhibit very low thermal expansion, high DOI on painted parts with good low temperature impact properties. ApplicationTPP 615 is de..
Tensile Strength, Yield 13.8 MPa
2000 psi
ISO 527-1/2
CTC X-PRO TF 1020 GP Polypropylene Homopolymer, 20% Talc Filled
X-PRO TF 1020 GP is a 20% talc reinforced polypropylene homopolymer. It has applications in general purpose industrial, automotive, consumer, and construction.Data provided by Composite Technologies..
Tensile Strength, Yield 13.8 MPa
2000 psi
ISO 527-1/2
CTC X-PRO TF 1040 GP Polypropylene Homopolymer, 40% Talc Filled
X-PRO TF 1040 GP is a 40% talc reinforced polypropylene homopolymer and made of 98% recycled content. It has applications in: automotive, industrial, construction, consumer and lawn & garden produc..
Tensile Strength, Yield 13.8 MPa
2000 psi
50 mm/min cross speed; ASTM D638
DuPont™ Surlyn® 9910 Ionomer Resin, Zinc
Surlyn® 9910 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
ExxonMobil LDPE LD 157CW Wire & Cable Low Density Polyethylene Resin
Product Description: LD 157CW is a medium density LDPE recommended for the production of Low Voltage power cable insulation, using the on-step silane cross0linking technology. The grade contains a h..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
ExxonMobil LLDPE LL 4004EL Wire & Cable Linear Low Density Polyethylene Resin (European Grade)
Product Description: LL 4004EL is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. Sufficient Cu-inhibitor shoul..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D638
ExxonMobil LLDPE LL 6301XR Molding Linear Low Density Polyethylene Resin (European Grade)
Product Description: LL 6301 series are medium flow LLDPE grades, with a relatively molecular weight, resulting in molded articles which are very tough and exhibit excellent environmental stress cra..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D-638
Axiall EX 3154 Plenum Flexible PVC
Non-lead stabilized CAT 3 plenum jacket. Recommended for up to 25 pair, unshielded.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D-638
Axiall 10640 Wire & Cable Flexible PVC
Non-lead stabilized general purpose, highly flexible jacket compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D-638
Axiall 14771 Wire & Cable Flexible PVC
General purpose jacketing compound with good low temperature properties. Recommended for a maximum service temperature of 75°C.Information provided by Georgia GulfGeorgia Gulf became Axiall Corpor..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D-638
Axiall 8710 Moldings & Extrusions Flexible PVC
Low gravity extrusion compound with excellent low temperature properties. Designed for use in weatherstrips and flexible gaskets. Excellent for co-extrusion with rigid PVC.Information provided by ..
Tensile Strength, Yield 13.8 MPa
2000 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Atomite Whiting Filler
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield 13.8 - 31.0 MPa
2000 - 4500 psi
Average value: 19.7 MPa Grade Count:16
Overview of materials for Medium Density Polyethylene (MDPE), Extruded
This property data is a summary of similar materials in the MatWeb database for the category "Medium Density Polyethylene (MDPE), Extruded". Each property range of values reported is minimum and max..
Tensile Strength, Yield 13.8 MPa
2000 psi
TM R050-36
Resinlab® EP965LVLX Clear Unfilled Electronic Grade Epoxy Encapsulant
Resinlab™ EP965LVLX Clear is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It cures at room temperature to a tough, semi-rigid polymer. It has ..
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D-638
Axiall 8705 Moldings & Extrusions Flexible PVC
General purpose PVC extrusion compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield 13.8 MPa
2000 psi
ASTM D-638
Axiall 8741 Moldings & Extrusions Flexible PVC
A low gravity general purpose extrusion compound recommended for use in weatherstrips, screen spline, extruded shapes and flexible gaskets.Information provided by Georgia GulfGeorgia Gulf became Axi..
Tensile Strength, Yield 13.8 MPa
2000 psi
At 50 mm/min; ASTM D638
Borealis Borstar® HE6063 Natural Bimodal HD Polyethylene Compound for Jacketing of Communication and Power Cables
Borstar HE6063 is a natural, colorable, bimodal, high-density polyethylene compound, produced using the Borstar process, for jacketing of power and telecommunications cables. It is characterized by..
Tensile Strength, Yield 13.8 - 52.0 MPa
2000 - 7540 psi
Average value: 26.6 MPa Grade Count:35
Overview of materials for Polypropylene with 10% Calcium Carbonate (CaCO3) Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Calcium Carbonate (CaCO3) Filler". Specific grades with primary filler content be..