Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 7.20 - 10.8 MPa | 1040 - 1570 psi | ±20% change after 168 hours @ 70°C; ASTM D412 |
Precision Polymer Engineering S50K Silicone Rubber Silicone Rubber, 45-55 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Federal.. |
|||
Tensile Strength, Yield | 7.20 - 10.8 MPa | 1040 - 1570 psi | ±20% change after 168 hours @ 70°C; ASTM D412 |
Precision Polymer Engineering S60K Silicone Rubber Silicone Rubber, 56-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Federal.. |
|||
Tensile Strength, Yield | 7.20 - 10.8 MPa | 1040 - 1570 psi | ±20% change after 168 hours @ 70°C; ASTM D412 |
Precision Polymer Engineering S70H Silicone Rubber White Silicone Rubber, 68-78 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States F.. |
|||
Tensile Strength, Yield | 4.00 - 10.8 MPa | 580 - 1570 psi | Average value: 7.34 MPa Grade Count:21 |
Overview of materials for Ethylene Acrylic Acid This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Acrylic Acid". Each property range of values reported is minimum and maximum values of appropri.. |