- Polymer Property : Tensile Strength, Yield = 4640 psi
Polymer Property : Tensile Strength, Yield = 4640 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-1, -2 |
| LyondellBasell Moplen HP400N Polypropylene Homopolymer Description: HP400N is a high flow homopolymer with a conventional molecular weight distribution and is formulated with a general-purpose additive package. HP400N is designed for injection molding a.. |
|||
| Tensile Strength, Yield | 32.0 MPa @Strain 0.200 %, Temperature 1093 °C |
4640 psi @Strain 0.200 %, Temperature 1999 °F |
|
| Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE... |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON FD000 PE LNP* STAT-KON* FD000 is an unfilled Polyethylene. Added feature of this grade is: Electrically Conductive. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 2 in/min; ASTM Test |
| Styrolution Terblend® N NM-11 ABS/PA6 (Conditioned) Terblend N NM-11 is an ABS/PA6 blend combining very high impact strength, even at low temperatures, with an excellent processability and surface appearance.Information provided by STYROLUTION, which.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl HIPS3191 PS This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Europe-Africa-Middle East) High modulus/impact/heat PPE+PP. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp MK001AS PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MK001AS is a compound based on Polypropylene resin containing Mineral. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Total PPH 3847MR Polypropylene, Radiation Resistant - Clarified - High Flow for Injection Molding TOTAL Petrochemicals Polypropylene 3847MR offers good processability, excellent clarity, good toughness and good resistance to typical levels of gamma radiation used to sterilize polypropylene.Easy .. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
| Total PPH 7060 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 7060 is homopolymer.ApplicationATOFINA Polypropylene PPH 7060 is intended for the injection molding of packaging containers, toys, domestic appliances, garden furniture and.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2 |
| Total PPM H350 Polypropylene, Homopolymer Medical Grade Polypropylene PPM H350 is a homopolymer with a Melt Flow Index of 35 g/10 min recommended for the manufacture of medical packaging and medical devices, to the exclusion of implants.Polypropylene PPM.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | |
| TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR Fumed Silica - Wacker HK N20 MILLATHANE E34 is a high performance polyether polyurethane rubber for applications requiring: high abrasion resistance, low temperature flexibility, ozone resistance, oil and fuel resistance, outst.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
| A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50mm/min; ISO 527-2 |
| Borealis BS4641 High Density Polyethylene BS4641 is a bimodal high-density polyethylene homopolymer. Because of its excellent organoleptic properties, this grade is especially suitable for blow molding of bottles for food applications. App.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
| A. Schulman PP 3466-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3466-01 is a homopolymer polypropylene with the addition of antistatic. This product enhances processing with fast cycle times in injection molding.ApplicationPP 3466-01.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2/50 |
| ExxonMobil Exxtral™ HMU 405 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with high heat ageing resistance, high transparency, low color and low discoloration for contact with hot water, hot air and detergent.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-2/50 |
| ExxonMobil Exxtral™ LNT 010 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with high heat ageing resistance, high transparency, low color and low discoloration for contact with hot water, hot air and detergent.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 2.0 in/min; ASTM D638 |
| ExxonMobil PP5341E1 Polypropylene Homopolymer Product Description: A low melt flow rate that provides high melt strength and resistance to softening at elevated temperature.Availability: North America Features:Low FlowUses: Automotive Applic.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | molded and tested in accordance with ASTM D 4101; ASTM D638 |
| Dow 5D98 Polypropylene Resin DOW 5D98 is intended for use in oriented polypropylene (OPP) film processes.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® LC6601 BK551 Nylon 612
(Unverified Data**) Plasticized Toughened Polyamide 612 Developed for Extrusion Information provided by DuPont Performance Polymers |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO R527 |
| Arkema Group Orgalloy® LE 60 LM Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0334W30L1 Wollastonite Reinforced |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Carmel Olefins CAPILENE® M 45 F Polypropylene Homopolymer CAPILENE® M 45 F is a polypropylene homopolymer developed for the production of cast films. It is formulated with slip and anti-blocking agents. They show high gloss, high transparency and good sti.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 2 in/min; ASTM Test |
| BASF Ultramid® 8253 HS PA6 (Conditioned) Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 2 in/min; ASTM Test |
| BASF Ultramid® 8253 PA6 (Conditioned) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 2 in/min; ASTM Test |
| BASF Ultramid® 8350 HS BK-102 PA6 (Conditioned) Ultramid 8350 HS BK-102 is a type 6, black pigmented, impact modified graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness
combined with a.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
| Azoty Tarnow™ TARNOFORM 300 HI6 POM Rubber modified grade with very high impact strength and damping capacity.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO value at 50 mm/min. |
| BASF Capron® 8253 Impact Modified Nylon 6 (Conditioned)
(discontinued **) Capron 8253 is an unfilled type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Capron 8253 HS) and/or pigmented versions.. |
|||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL FN215Z PPE+HIPS (Asia Pacific) PPE + PS, FR foam molding grade |
|||