Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 35.8 MPa | 5190 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ HTX Ultra LA426G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss version of Geon HTX Ultra LA426Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426G Black 2880.Information provided by Pol.. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | |
Ineos ABS Lustran® LGM Key Features:UnfilledSuitable processing methods:Injection molding |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | 2 in/min (50 mm/min); ASTM D-638 |
Ineos H00G-00 Polypropylene Homopolymer A polypropylene homopolymer produced by Ineos utilizing catalyst technology. This material meets the Food and Drug Administration requirements of 21CFR 177.1520. Homopolymer H00G-00 meets certain .. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
IRPC Polimaxx Polene 1111NX TA8 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER WITH 40% TALCUM REINFORCED HIGH STIFFNESSAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | Elastic Limit |
Wolf Kunststoff ZEDEX® ZX-750V5T A9T Polymer Alloy Main Characteristics: Hard; Stiff; Tough; High dimensional stability; High fatigue strength; High weather resistance; Good fire behavior; Suitable for vacuum; Good machinability; Contains PTFE; Stre.. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers Diamaloy ABS VP-22 Flame Retardant ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers DIAMALOY VP22 Flame Retardant ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers DIAMALOY VP22 NATURAL 1001B Blow Molding Grade, Flame Retardant ABS Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |