Polymer Property : Tensile Strength, Yield = 87.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	87.0 MPa @Strain 0.200 %, Temperature 980 Â°C	12600 psi @Strain 0.200 %, Temperature 1800 Â°F
Haynes 263Â® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle..
Tensile Strength, Yield	87.0 MPa	12600 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific) LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Strength, Yield	87.0 MPa	12600 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Tensile Strength, Yield	87.0 MPa	12600 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific) LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.
Tensile Strength, Yield	87.0 MPa	12600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP LX82803 PEEK (Europe-Africa-Middle East) LNP* LUBRICOMP* LX82803 is a compound based on Polyetheretherketone resin containing Proprietary Lubricant. Added features include : Internally Lubricated.
Tensile Strength, Yield	87.0 MPa	12600 psi	Type 1A, 50 mm/min; ISO 527-2
Solvay Specialty Polymers AvaSpireÂ® AV-621 Polyaryletherketone (PAEK) AvaSpireÂ® AV-621 is an unreinforced polyaryletherketone (PAEK) that offers improved ductility and impact strength relative to PEEK while retaining most of the key performance attributes of PEEK. ..
Tensile Strength, Yield	87.0 MPa	12600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W..
Tensile Strength, Yield	87.0 MPa	12600 psi	ASTM-D638
Polyram RamSter PF329G4 PBT, 20% Glass Fiber, Flame Retardant 20% Glass fiber reinforced, halogen free flame retardant PBT for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield	87.0 MPa	12600 psi	dry; ISO 527-1/-2
DSM Novamid® 1010C2 PA6 Easy Molding Grade
Tensile Strength, Yield	87.0 MPa	12600 psi	ISO 527
Azoty Tarnow™ TARNOFORM 300 GF3 POM 15% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A...
Tensile Strength, Yield	87.0 MPa	12600 psi	ISO 527-2/1A/50
Solvay Specialty Polymers AvaSpire® AV-621 Polyaryletherketone (PAEK) (Unverified Data**) AvaSpire AV-621 is an unreinforced polyaryletherketone (PAEK) that offers improved ductility and impact strength relative to PEEK while retaining most of the key performance attributes of PEEK. The ..
Tensile Strength, Yield	87.0 MPa	12600 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® VX4510 PBT (Europe-Africa-Middle East) VALOX VX4510 is a flame retarded, 10% glassfiber reinforced injection moulding PBT resin.
Tensile Strength, Yield	87.0 MPa @Strain 0.200 %, Temperature 1093 °C	12600 psi @Strain 0.200 %, Temperature 1999 °F
Haynes 230® alloy, as cast vacuum investment casting Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Tensile Strength, Yield	87.0 MPa	12600 psi	ISO 527
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Strength, Yield	87.0 MPa	12600 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).
Tensile Strength, Yield	87.0 MPa	12600 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).
Tensile Strength, Yield	87.0 MPa	12600 psi	SABIC - Japan Method
SABIC Innovative Plastics Valox® VSR4150 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.