Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 |
Quadrant EPP Fluorosint® HPV PTFE + additives, bearing grade, compression moulded (ISO Data) FDA compliant Fluorosint HPV is a high performance Fluorosint bearing grade, optimized for high pressure-velocity capabilities and very low wear. Fluorosint HPV was developed for bearing application.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Faradex MS002P PP (Asia Pacific) LNP* Faradex* MS002P is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, Exceptional Processi.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Faradex MS002P PP (Europe-Africa-Middle East) LNP* Faradex* MS002P is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, Exceptional Processi.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Faradex MS003XXC PP (Europe-Africa-Middle East) LNP* Faradex* MS003XXC is a compound based on Polypropylene resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding.This data was supplied by SABIC-IP for.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1[mm/min]; ISO 527-1/2 |
Akro-Plastic Akromid® S31 (3484) PA 6.10 Conditioned
(discontinued **) A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | |
LyondellBasell Lupolen® 5621 D HDPE Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® AC 30 000000 Nylon 66 PA 66, injection molding-grade, non-reinforced, higher notched impact strength than A 30 / A 31 in the dry and conditioned stateApplication Examples: plug connectors, cable binders, cable clips, par.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® BC 40 SR2 000000 Nylon 6 PA 6 injection molding grade, high viscosity, non-reinforced, higher notched impact strength than BC 30, impact-modified |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
Styrolution Styrolux T SBC Styrolux T is a new developmental, clear and tough styrene-butadiene copolymer (SBC) designed specifically for high performance film extrusion and shrink film applications. Styrolux T has been devel.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1 mm/min; ISO 527 |
Styron INSPIREâ„¢ TF0808S(U) Polypropylene TF0808S(U) is a talc filled PP exhibiting high impact resistance and a high stiffness. It is particularly well suited for low wall thickness bumper skins. INSPIRE TF0808S for painted parts INSPIRE .. |
|||
Tensile Modulus | 1.20 GPa @Temperature 23.0 °C |
174 ksi @Temperature 73.4 °F |
1mm/min; ISO 527-2/1A/1 |
SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend Polymer blend HIPS/PE. High toughness, very good tensile properties and environmental stress cracking resistance. Processed mainly by extrusion and thermoforming. Production of sheets and films, tec.. |
|||
Tensile Modulus | 1.20 - 1.40 GPa | 174 - 203 ksi | TD; ISO 527-3 |
Borealis BorPURE™ RB501BF Polypropylene Copolymer BorPure™ RB501BF is a random copolymer. Applications: BorPure™ RB501BF has been developed especially for applications like: food packaging, over wrap film, label film, and shrink film. Additives.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527-2 |
Borealis RJ900MO Polypropylene Random Copolymer RJ900MO is a polypropylene random copolymer with high melt flow and good transparency. Products originating from this grade have excellent transparency and gloss, and good balance of stiffness and .. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 |
Unitika EX-1020K PA6, Conditioned Conducting nylonInformation provided by Unitika Ltd. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6000 HWCP Nylon 6, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6000 SCP Nylon 6, Finely Crystalline, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6000 SUVCP Nylon 6, Finely Crystalline, UV Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600 PA-66-HWV0CP UL-Licensed Nylon 66, Flame Protection, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | Secant; ISO 527-2 |
ExxonMobil Exxtral™ BMU 130 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by a good stiffness/toughness balance for automotive exterior applications such as bumper fascia.Availability: Europe F.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 100ST BK602 Acetal (POM)
(Unverified Data**) Super Toughened High Viscosity Acetal Homopolymer Delrin 100ST BK602 is a super tough high viscosity acetal homopolymer grade with superior impact resistance. It is designed for highly stressed part.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® E51HSB NC010 Nylon 66
(Unverified Data**) Unreinforced Heat Stabilized High Viscosity Polyamide 66 Zytel E51HSB NC010 is a high molecular weight heat stabilized polyamide 66 resin for injection molding and extrusion.Information provided by .. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | cond.; DIN 53 457 |
Hippe PA 46 Nylon 46 PA 46 is primarily used in higher temperature ranges where stiffness, creep resistance, continuous heat stability and fatigue strength are required. Therefore PA 46 is suitable for high quality app.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FG53 NC010 Nylon 66
(Unverified Data**) Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 1000-11 NF2001 PA66 (Conditioned) Ultramid 1000-11 NF2001 is a general purpose nylon 6/6. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 1000-2 NF2001 PA66 (Conditioned) Ultramid 1000-2 NF2001 is a general purpose PA6/6. |
|||
Tensile Modulus | 1.20 GPa @Temperature 120 °C |
174 ksi @Temperature 248 °F |
ISO Data |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527 |
BASF Ultramid® NBX-0025 NF2001 PA66 (Conditioned) Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
Azdel SuperLite® SL551200-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551200-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527-2 |
Borealis Daplen™ EF103AE Polypropylene TPO Compound Daplen™ EF103AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, high melt flow rate an.. |