Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 1.20 GPa | 174 ksi | |
Plastcom SLOVALEN PQ 81 T 10 PP, 10% mineral filling FeaturesModified PP for injection moulding with the content of 10% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | |
Radici Radilon® S 35FL (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Modulus | 1.20 GPa @Temperature 23.0 °C |
174 ksi @Temperature 73.4 °F |
dry as moulded; ISO 527-2/1 |
PolyOne Bergamid™ A700 TM-YF Polyamide 66 (Nylon 66) Information provided by PolyOne |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 |
DSM Akulon® K230-HPV8 Impact Modified Nylon 6 (European Grade) (Dry)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
Iran Petrochemical (PCC) EX 2 HF 7750 M High Density Polyethylene EX2 is a high density polyethylene with 1-Butene as co monomer. It has good rigidity and medium molar mass. Applications: monofilaments, ropes, yarns.Information provided by Iran Petrochemical Com.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
Iran Petrochemical (PCC) EX 2 S HF 7750 M2 High Density Polyethylene EX2S is a high density polyethylene with 1-Butene as co monomer. It is medium molar mass, low density grade with a narrow molar mass distribution, high rigidity, good tear strength. Applications: .. |
|||
Tensile Modulus | 1.20 GPa @Temperature 23.0 °C |
174 ksi @Temperature 73.4 °F |
1mm/min; ISO 527-2/1A/1 |
SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend Polymer blend HIPS/PE. High toughness, very good tensile properties and environmental stress cracking resistance. Processed mainly by extrusion and thermoforming. Production of sheets and films, tec.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527-2 |
Borealis Borcom™ WE007AE Polypropylene Borcom™ WE007AE is a polypropylene microcomposite intended for injection molding. The product is available in natural color. This material has an excellent balance between impact strength and stif.. |
|||
Tensile Modulus | 1.20 - 1.40 GPa | 174 - 203 ksi | TD; ISO 527-3 |
Borealis BorPURE™ RB501BF Polypropylene Copolymer BorPure™ RB501BF is a random copolymer. Applications: BorPure™ RB501BF has been developed especially for applications like: food packaging, over wrap film, label film, and shrink film. Additives.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 |
Unitika EX-1020K PA6, Conditioned Conducting nylonInformation provided by Unitika Ltd. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | At 1 mm/min; ISO 527-2 |
Borealis Daplen™ VB4411 TPO Compound Daplen VB4411 is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen VB4411 is a material with excellent impact /stiffness ratio. Thanks to its low th.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ASTM-D790 |
Polyram RamOfin PPC501 Polypropylene, Flame Retardant Flame retardant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600 PA-66-HWV0CP UL-Licensed Nylon 66, Flame Protection, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600/508 HWUVCP Nylon 66, Impact Modified, UV Stabilized, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | Through Plane Direction |
Cymat A35620SC 040SS Stabilized Aluminum Foam Description: Cymat A35620SC 040SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.4 g/cm3. The mechanical properties of SAF make it .. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 3959 nat PA610 Product description: Grilamid XE 3959 natural is a high viscosity Polyamide 610 especially suitable for extrusion applications. This PA610 product is to a large extent based on renewable raw materia.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4071 black 9992 PA612 Product description: Grilamid XE 4071 BLACK 9992 is an impact modified unreinforced high viscosity polyamide 612 (PA612) extrusion grade with superior heat and hydrolysis resistance. Compared to sta.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4128 black 9221 PA610 Product description: Grilamid XE 4128 black 9221 is a modified high viscosity Polyamide 610 for extrusion as well as injection molding. A characteristic of tubes made out of this material is the hig.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-2 |
Domo 2300K Polypropylene Copolymer Information provided by Domo. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® FG53 NC010 Nylon 66
(Unverified Data**) Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1 mm/min; ISO 527 |
Eurostar Starflam MX06089 PP, Flame Retardant, Injection Molding Starflam MX06089 is an Unfilled Flame Retardant Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® BS V0 PA6 Product description: Grilon BS V0 is an unreinforced, normal viscosity, self-extinguishing PA6 injection molding grade. Grilon BS V0 has the following important properties: Halogen and phosphorous-f.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ASTM D638 |
Aclo Accuguard Polypropylene HP1362V2CSL Homopolymer Flame Retardant Copper Stabilized |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527 |
BASF Ultramid® 1000-2 NF2001 PA66 (Conditioned) Ultramid 1000-2 NF2001 is a general purpose PA6/6. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527 |
BASF Ultramid® NBX-0025 NF2001 PA66 (Conditioned) Ultramid NBX-0025 NF2001 is a specialty, unfilled PA6/6. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | |
Plastcom SLOVALEN PQ 83 T 10 PP, 10% mineral filling FeaturesModified PP + EPDM for injection moulding with the content of 10% mineral filler. Increased rigidity, strength and thermal. Decreased shrinkage. Application in automotive, covers of car chas.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | At 1 mm/min; ISO 527-2 |
Borealis Daplen™ PB4432 TPO Compound Daplen PE4432 is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen PE4432 is a material with excellent impact /stiffness ratio. Thanks to its low th.. |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 |
BASF Ultraform® N2650 Z6 POM + PUR Description: Elastomer-modified injection molding grade for applications requiring highest impact strength together with low stiffness.Information provided by BASF |
|||
Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-2 |
Cathay PA56 Renewable Engineering Polyamide, 50% RH Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |