Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 3.62 GPa | 525 ksi | ASTM D638 |
Fiberfil® J-68/25/E/SD Polypropylene Copolymer, 25% Glass Fiber Reinforced, Chemically coupled, with static dissipation Information provided by FIBERFIL Engineered Plastics |
|||
Tensile Modulus | 3.62 GPa | 525 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA 6/12 (Asia Pacific) LNP* LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated. |
|||
Tensile Modulus | 3.62 GPa | 525 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA6.12 LNP LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant. |
|||
Tensile Modulus | 3.62 GPa | 525 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66 LNP* LUBRICOMP* RX05487 is a compound based on Nylon 66 containing 10% Aramid Fiber, 10% Lubricant. Added features of this material are: Low Warpage, Wear Resistant. |
|||
Tensile Modulus | 3.62 GPa | 525 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant. |
|||
Tensile Modulus | 3.62 GPa | 525 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant. |
|||
Tensile Modulus | 3.62 GPa | 525 ksi | Neat Resin |
Hexcel® Redux® HP655 Toughened BMI film Adhesive Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655.. |
|||
Tensile Modulus | 3.62 GPa | 525 ksi | ASTM D638 |
Quadrant EPP Quadrant Nylon 105 Black |