Polymer Property : Film Tensile Strength at Break, TD = 15.9 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	15.9 MPa	2300 psi	ASTM D882
NOVA Chemicals Novapol® LA-0219-A LDPE Foam Resin Features: Good heat sealing latitudeModerate toughnessEasy processability Applications: Industrial packagingLinersBlends with LLDPEFoam ArticlesInformation provided by Nova Chemicals
Film Tensile Strength at Break, TD	15.9 MPa	2300 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA952000 Low Density Polyethylene ApplicationsPETROTHENE NA 952 is a series of homopolymer resins especially designed for industrial and consumer packaging, and liner and bag applications. NA 952 has an excellent balance of process..
Film Tensile Strength at Break, TD	15.9 MPa	2300 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA952094 Low Density Polyethylene ApplicationsPETROTHENE NA 952 is a series of homopolymer resins especially designed for industrial and consumer packaging, and liner and bag applications. NA 952 has an excellent balance of process..
Film Tensile Strength at Break, TD	15.9 MPa	2300 psi	ASTM D882
Westlake EF608 Low Density Polyethylene Westlake EF608 is a high melt index LDPE resin suggested for thin gauge garment films and other films requiring excellent drawdown. The high melt index makes this material a good choice in compound..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi
Dow LDPE 501I Low Density Polyethylene, Clear Film Grade DOW LDPE 501I, a barefoot resin used for bakery film and other packaging applications that require optical clarity. This material complies with U.S.FDA regulation 21 CFR 177.1520(c) 2.1 for food con..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi
Dow LDPE 503A Low Density Polyethylene, Liner Film Grade DOW LDPE 503A resin is used for liner film and other packaging applications that require optical clarity. It contains medium levels of slip additive and low levels of antiblock additive. It complies..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M Scotch® 3743 High Tack Box Sealing Tape Scotch® Box Sealing Tape 3743 is a high-tack packaging tape used for box sealing, splicing, recouperage and other demanding packaging applications. This product has a heavy-duty, conformable backin..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M Scotch® 824 Pouch Tape Scotch® Pouch Tape 824 is a pressure-sensitive tape with a bright, orange boarder on all four edges, and a non-tack “see-through” central rectangle, which provides a quick, simple, highly visible..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M Scotch® 825 Pouch Tape Scotch® Pouch Tape 825 is a pressure-sensitive tape with a bright, orange boarder on all four edges, and a non-tack “see-through” central rectangle, which provides a quick, simple, highly visible..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M ScotchPad™ 830 Pouch Tape Pads 3M™ ScotchPad™ Pouch Tape Pads are pre-cut pressure-sensitive tapes with a sticky boarder and a printed, non-tack center section that comes either as a standard or custom printed pouch which is cl..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M ScotchPad™ 832 Pouch Tape Pads 3M™ ScotchPad™ Pouch Tape Pads are pre-cut pressure-sensitive tapes with a sticky boarder and a printed, non-tack center section that comes either as a standard or custom printed pouch which is cl..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M ScotchPad™ 832CP Pouch Tape Pads 3M™ ScotchPad™ Pouch Tape Pads are pre-cut pressure-sensitive tapes with a sticky boarder and a printed, non-tack center section that comes either as a standard or custom printed pouch which is cl..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M Scotch® 827 Pouch Tape Scotch® Pouch Tape 827 is a pressure-sensitive tape with a bright, orange boarder on all four edges, and a non-tack “see-through” central rectangle, which provides a quick, simple, highly visible..
Film Tensile Strength at Break, TD	15.9 MPa	2310 psi	ASTM D3759
3M ScotchPad™ 830CP Pouch Tape Pads 3M™ ScotchPad™ Pouch Tape Pads are pre-cut pressure-sensitive tapes with a sticky boarder and a printed, non-tack center section that comes either as a standard or custom printed pouch which is cl..
Film Tensile Strength at Break, TD	15.9 MPa	2300 psi	ASTM D882
ExxonMobil Optema® TC-114 Cast Ethylene Methyl Acrylate Product Description: Optema TC 114 is an ethylene methyl acrylate copolymer specifically formulated to offer extrusion and property performance for blown and cast film applications. It produces a so..
Film Tensile Strength at Break, TD	15.9 - 36.5 MPa	2300 - 5290 psi	Average value: 27.2 MPa Grade Count:7
Overview of materials for Ethylene-Methyl Acrylate Copolymer, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Film Grade". Each property range of values reported is minimum and m..