Overview of materials for Ethylene-Methyl Acrylate Copolymer, Film Grade

Category Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Ethylene-Methyl Acrylate Copolymer, Film Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Film Grade". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.930 - 0.948 g/cc
0.0336 - 0.0342 lb/in³
Average value: 0.940 g/cc Grade Count:8
Viscosity 1.10e+6 - 1.10e+6 cP

@Temperature 190 - 190 °C
1.10e+6 - 1.10e+6 cP

@Temperature 374 - 374 °F
Average value: 1.10e+6 cP Grade Count:1
1.10e+6 - 1.10e+6 cP

@Shear Rate 50.0 - 50.0 1/s
1.10e+6 - 1.10e+6 cP

@Shear Rate 50.0 - 50.0 1/s
Average value: 1.10e+6 cP Grade Count:1
Environmental Stress Crack Resistance >= 360 hour

@Temperature 50.0 - 50.0 °C
>= 360 hour

@Temperature 122 - 122 °F
Average value: 360 hour Grade Count:1
Methyl Acrylate Content 16.5 - 26.0 %
16.5 - 26.0 %
Average value: 19.3 % Grade Count:4
Melt Flow 0.400 - 9.00 g/10 min
0.400 - 9.00 g/10 min
Average value: 2.97 g/10 min Grade Count:14
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 350 - 596 %
350 - 596 %
Average value: 449 % Grade Count:7
Film Elongation at Break, TD 450 - 790 %
450 - 790 %
Average value: 584 % Grade Count:7
Secant Modulus, MD 0.0496 - 0.165 GPa
7.20 - 23.9 ksi
Average value: 0.108 GPa Grade Count:7
Secant Modulus, TD 0.0517 - 0.171 GPa
7.50 - 24.8 ksi
Average value: 0.105 GPa Grade Count:7
Elmendorf Tear Strength, MD 0.787 - 5.51 g/micron
20.0 - 140 g/mil
Average value: 4.32 g/micron Grade Count:5
Elmendorf Tear Strength, TD 3.94 - 7.48 g/micron
100 - 190 g/mil
Average value: 5.68 g/micron Grade Count:5
Dart Drop 3.90 - 10.2 g/micron
99.1 - 260 g/mil
Average value: 7.35 g/micron Grade Count:3
Dart Drop Test 5.90 - 370 g
0.0130 - 0.816 lb
Average value: 141 g Grade Count:4
Seal Strength 1400 - 2700 g/25 mm
1400 - 2700 g/in
Average value: 2280 g/25 mm Grade Count:4
Hot Tack Strength 1400 - 1800 g/25 mm
1400 - 1800 g/in
Average value: 1720 g/25 mm Grade Count:5
Film Tensile Strength at Break, MD 20.0 - 38.6 MPa
2900 - 5600 psi
Average value: 27.6 MPa Grade Count:7
Film Tensile Strength at Break, TD 15.9 - 36.5 MPa
2300 - 5290 psi
Average value: 27.2 MPa Grade Count:7
Thermal Properties Metric English Comments
Melting Point 72.0 - 104 °C
162 - 219 °F
Average value: 89.8 °C Grade Count:14
Vicat Softening Point 45.0 - 95.0 °C
113 - 203 °F
Average value: 73.0 °C Grade Count:13
Optical Properties Metric English Comments
Haze 2.50 - 3.50 %
2.50 - 3.50 %
Average value: 2.92 % Grade Count:4
Gloss 55.0 - 82.0 %
55.0 - 82.0 %
Average value: 65.5 % Grade Count:4
Processing Properties Metric English Comments
Nozzle Temperature 180 - 300 °C
356 - 572 °F
Average value: 214 °C Grade Count:9
Melt Temperature 175 - 315 °C
347 - 599 °F
Average value: 220 °C Grade Count:9