ExxonMobil Optema® TC-114 Cast Ethylene Methyl Acrylate

Category Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Film Grade
Manufacturer Exxon Chemical
Trade Name Optema®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Optema® TC-114 Cast Ethylene Methyl Acrylate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Optema TC 114 is an ethylene methyl acrylate copolymer specifically formulated to offer extrusion and property performance for blown and cast film applications. It produces a soft, elastic film with good handling characteristics without additional additives. Optema TC 114 can produce film under 1.0 mil thickness. Availability: Latin America, North America and South America Additive: Anitblock: 14000 ppmSlip: 3000 ppmThermal Stabilizer: YesApplications: Disposable GlovesHospital DrapesUpholstery FilmData provided by the manufacturer, Exxon Chemical.
Physical Properties Metric English Comments
Density 0.947 g/cc
0.0342 lb/in³
Exxon Method
Methyl Acrylate Content 18 %
18 %
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 3.20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 1400 ppm
1400 ppm
Slip Level 3000 ppm
3000 ppm
[ppm]
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 790 %
790 %
ASTM D882
Elmendorf Tear Strength MD 90 g
90 g
ASTM D1922
Elmendorf Tear Strength TD 350 g
350 g
ASTM D1922
Dart Drop Test 180 g
0.397 lb
ASTM D1709A
Film Tensile Strength at Break, MD 22.1 MPa
3200 psi
ASTM D882
Film Tensile Strength at Break, TD 15.9 MPa
2300 psi
ASTM D882
1% Secant Modulus, MD 55.8 MPa
8100 psi
ASTM D882
1% Secant Modulus, TD 56.5 MPa
8200 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 81.0 °C
178 °F
Exxon Method
Vicat Softening Point 57.2 °C
135 °F
ASTM D882