Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 41.2 MPa @Thickness 3.20 mm |
5970 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical HIPS 403AF PS, Flame Retardant Description: Injection Molding, PS, Flame RetardantApplication: Electric Parts Requiring Flame RetardancyCAS: 9003-55-8, 21850-44-2 and 1309-64-4Information provided by LG Chemical |
|||
Flexural Yield Strength | 41.2 MPa @Thickness 6.40 mm |
5970 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL HI5204G PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 26221-73-8 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 41.2 MPa | 5980 psi | 15 mm/min; ASTM D790 |
LG Chemical 40 AF Flame Retardant HIPS High impact, Safety standards: listed with UL CSA, and classified according to IEC 707, Meet requirements for flammability, mechanical and electrical properties, Applications include televisions, VT.. |
|||
Flexural Yield Strength | 41.2 MPa @Thickness 6.40 mm |
5970 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL HM5204 PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 41.2 MPa | 5970 psi | ASTM D790 |
IRPC Polimaxx Polene 1196NN Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER UNREINFORCED, CONTAIN FLAME RETARDANT, UL 94 V-2 APPROVAL, HIGH IMPACT STRENGTHAPPLICATIONS: INJECTION MOLDING FOR ELECTRICAL APPLIANCES |
|||
Flexural Yield Strength | 41.2 MPa @Temperature 300 °C |
5970 psi @Temperature 572 °F |
ASTM D790 |
UBE UPIMOL® S High Heat Polyimide Shape Description: Ube's UPIMOL is an exceptionally heat-resistant polyimide Shape. This product has the same molecular structure as UPILEX, an ultra-high heat-resistant polyimide film developed by Ub.. |
|||
Flexural Yield Strength | 41.2 MPa | 5970 psi | ASTM D790 |
Diapolyacrylate Acrypet® IR H70 Impact Modified PMMA Acrypet® is a registered trade mark of Diapolyacrylate Company Limited. Information provided by Dayson Polymers. |
|||
Flexural Yield Strength | 41.2 - 105 MPa | 5970 - 15200 psi | Average value: 69.8 MPa Grade Count:110 |
Overview of materials for Acrylic, Impact Modified, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified, Molded". Each property range of values reported is minimum and maximum values .. |