Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 47.1 - 579 MPa | 6830 - 84000 psi | Average value: 73.4 MPa Grade Count:112 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded". Each property range of values reported is .. |
|||
Flexural Yield Strength | 47.1 - 92.2 MPa | 6830 - 13400 psi | Average value: 67.2 MPa Grade Count:34 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded". Each property range of values reported is m.. |
|||
Flexural Yield Strength | 47.1 MPa | 6830 psi | 15 mm/min; ASTM D790 |
LG Chemical 65IH HIPS High impact, Extrusion, Balanced mechanical properties, Good surface appearance with high gloss, Conforming to FDA CFR 177.1640, Excellent processability, Applications include refrigerator food tray.. |
|||
Flexural Yield Strength | 47.1 MPa @Thickness 3.20 mm |
6830 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical HI100X ABS, High Impact, Semi-Transparency, Flexible Feature: Injection Molding, High Impact, Semi-Transparency, FlexibleApplication: Artificial Nails, Miscellaneous Goods)CAS No. 9010-94-0Information provided by LG Chemical |
|||
Flexural Yield Strength | 47.1 MPa @Thickness 3.20 mm |
6830 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical HIPS 65IHE PS, Impact Modified Description: Injection Molding, PS, General Purpose, Impact ModifiedApplication: Refrigerator Tray, Food Tray, Refrigerator Door LinerCAS: 9003-55-8Information provided by LG Chemical |