Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 58.8 - 530 MPa | 8530 - 76900 psi | Average value: 261 MPa Grade Count:531 |
Overview of materials for Polyphthalamide (PPA) This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 3.20 mm |
8530 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID HI5006A(W) PA6/ABS, High Impact, Good Dimensional Stability Feature: Injection Molding, PA6/ABS, High Impact, Good Dimensional StabilityApplication: Pipe Fitting, Electrical and Electronic partsCAS No. 25038-54-4, 9003-56-9 and 9003-54-7Information provided .. |
|||
Flexural Yield Strength | 58.8 MPa | 8530 psi | ASTM D790 |
IRPC Polimaxx Polene 2311LCX GA4 Polypropylene Compound CHARACTERISTICS: POLYPROPYLENE BLOCK COPOLYMER WITH 20% GLASS FIBRE REINFORCED, HIGH IMPACT STRENGTH, HIGH MECHANICAL STRENGTH, HIGH STIFFNESS, LOW SHRINKAGEAPPLICATIONS: INJECTION MOLDING FOR AUTOP.. |
|||
Flexural Yield Strength | 58.8 MPa | 8530 psi | ASTM D790 |
Samyang Trimma® SD6320P PMMA, Translucent High scratch resistance; stability against weak acids, strong acids, weak alkalis and inorganic salts.Information provided by Samyang. |
|||
Flexural Yield Strength | 58.8 MPa @Temperature 260 °C |
8530 psi @Temperature 500 °F |
ASTM D790 |
UBE UPIMOL® R Polyimide Shape Description: Ube's UPIMOL is an exceptionally heat-resistant polyimide Shape. This product has the same molecular structure as UPILEX, an ultra-high heat-resistant polyimide film developed by Ub.. |
|||
Flexural Yield Strength | 58.8 MPa | 8530 psi | ASTM D790 |
Cheng Yu Plastic PP230H TALC 30 Polypropylene, 30% Talc, High Heat |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron AN450N Flame Retardant ABS Flame Retardant- V0 at 2.0mmInformation provided by Bhansali |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-11BM ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-11BM ABS Injection Molding Grade High Impact Strength, Medium Flow, High Fatigue ResistanceInformation provided by Bhansali |
|||
Flexural Yield Strength | 58.8 MPa | 8530 psi | ASTM D790 |
Cheng Yu Plastic IPS610BK Electric Conducting HIPS, Extrusion |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE32 FR IS15061 Flame Retardant ABS Flame Retardant- IS 15061 conformedInformation provided by Bhansali |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron AN450N Flame Retardant ABS Flame Retardant- V0 at 2.0mmInformation provided by Bhansali |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
ASTM D-790 |
Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Flexural Yield Strength | 58.8 MPa @Thickness 6.40 mm |
8530 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
Bhansali Engineering Abstron SE32 FR IS15061 Flame Retardant ABS Flame Retardant- IS 15061 conformedInformation provided by Bhansali |