- Polymer Property : Tensile Strength, Ultimate = 120000 psi
Polymer Property : Tensile Strength, Ultimate = 120000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 830 MPa @Temperature -80.0 °C |
120000 psi @Temperature -112 °F |
EN min; EN 10002-5 |
| Outokumpu 4307 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
| Tensile Strength, Ultimate | 825 MPa | 120000 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4565 High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
| Tensile Strength, Ultimate | 830 MPa | 120000 psi | Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu SAF 2507® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| Pacific Sintered Materials FX-232-T(HT) Infiltrated High Carbon Steel Powdered Metal Good strength, shock resistance and hardenability. Moderate tolerance control.Equivalent MPIF Specification: FX-1008-110HTAll information provided by Pacific Sintered Metals. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| PSM Industries Pacific Sintered Metals Infiltrated High Carbon Steel FX-232-T(HT) Powdered Metal Good strength, shock resistance and hardenability, Moderate tolerance control Equivalent MPIF Specification: FX-1008-110HTInformation Provided by Pacific Sintered Metals, a division of PSM Industri.. |
|||
| Tensile Strength, Ultimate | >= 827 MPa | >= 120000 psi | |
| PSM Industries PolyAlloys WNF-7129 Tungsten Heavy Alloy Mil. T-21014 Class 1, SAE-AMS-T-21014 Class 1, AMS 7725 B, ASTM-B-777-87 Class 1Information Provided by PolyAlloys, a division of PSM Industries |
|||
| Tensile Strength, Ultimate | 830 MPa | 120000 psi | |
| Polyimide Fiber |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| Hogen HM1100 Tungsten-Based Metal Mil Spec T-21014D Class 1; ASTM B-777-99 Class 1; SAE Aero Material Spec (AMS) 7725C; AMS T-21014 Class 1. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers hig.. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| Hogen HM3050 Tungsten-Based Metal Mil Spec T-21014D Class 3; ASTM B-777-99 Class 3; AMS T-21014 Class 3. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers high thermal conductivity and a low CTE.. |
|||
| Tensile Strength, Ultimate | 828 MPa | 120000 psi | |
| Kennametal Stellite Stellite® 31 PM with P/M Processing; heat treated at 93°C (200°F) and water quenched Typical applications include, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc. |
|||
| Tensile Strength, Ultimate | 828 MPa @Temperature 538 °C |
120000 psi @Temperature 1000 °F |
|
| Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
| Tensile Strength, Ultimate | 825 - 965 MPa | 120000 - 140000 psi | |
| Materion Brush 60™ HT Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 96%Stress Relaxation afte.. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| Mi-Tech Metals HD17D Tungsten-Based Metal Mil Spec T-21014D Class 1; ASTM B-777-99 Class 1; ASTM B-777-07 Class 1; SAE Aero Material Spec (AMS) 7725C; AMS T-21014 Class 1. Slightly Magnetic.Manufactured by powder metallurgy methods. The t.. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | 621°C Temper Temperature |
| Latrobe Lescalloy® 16NCD13 VAC-ARC High Strength Alloy Steel 16NCD13 VAC-ARC is a premium quality low alloy, carburizing casehardenable vacuum arc remelted steel which takes its name from the French industry designation. In the carburized condition, its high .. |
|||
| Tensile Strength, Ultimate | 830 MPa | 120000 psi | |
| Haynes Hastelloy® W alloy, gas tungsten arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| Tensile Strength, Ultimate | 827 MPa @Temperature 427 °C |
120000 psi @Temperature 801 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Ultimate | 825 MPa | 120000 psi | |
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Tensile Strength, Ultimate | 830 MPa @Temperature 95.0 °C |
120000 psi @Temperature 203 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| Special Metals Electroformed Nickel, 6 Micron (0.24 mil) Foil, As-Electroformed Data provided by the manufacturer, Special Metals. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | Annealed |
| Universal Wire Works 5Al-2.5Sn (AMS 4953) Titanium Alloy Filler Metal Universal Ti 5Al-2.5Sn titanium alloy is easily joined with the gas tungsten arc, gas metal arc or resistance welding processes. 100% joint efficiency can be obtained provided proper shielding proce.. |
|||
| Tensile Strength, Ultimate | >= 828 MPa | >= 120000 psi | |
| TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) Aged Cold Workable Medium Strength Alloy. UTS, TYS, and elongation data below are specific to aged material; other specific condition entries are also available in MatWeb.Features: Cold formable and we.. |
|||
| Tensile Strength, Ultimate | >= 825 MPa | >= 120000 psi | L, LT and ST Directions |
| TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 2.50 - 4.00 in Rod or Thickness; Per ASTM F136) Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | cold worked |
| CMW® ELKONIUM 306 platinum based alloy Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (.. |
|||
| Tensile Strength, Ultimate | 827 MPa @Temperature -129 °C |
120000 psi @Temperature -200 °F |
Longitudinal |
| Carpenter 20Cb-3® Stainless Steel Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re.. |
|||
| Tensile Strength, Ultimate | 827 - 965 MPa | 120000 - 140000 psi | |
| Ametek AM 388™ Alloy (UNS C72650) TM06 Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and.. |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | Solution Annealed |
| ATI Allegheny Ludlum Altemp® 263 Nickel-Based alloy Characteristics: high strength up to 1500°F, oxidation resistance up to 2000°FInformation provided by Allegheny Ludlum |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | Beta Quenched |
| ATI Wah Chang Tiadyne™ 3510 Capable of being surface hardened to depths that produce very high wear resistance. Produced by traditional metallurgical processing, not special treatments.Information provided by ATI Wah Chang |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Tensile Strength, Ultimate | >= 827 MPa | >= 120000 psi | |
| PSM Industries PolyAlloys WNF-5421 Tungsten Heavy Alloy Mil. T-21014 Class 2, SAE-AMS-T-21014 Class 2, ASTM-B-777-87 Class 2Information Provided by PolyAlloys, a division of PSM Industries |
|||
| Tensile Strength, Ultimate | 827 MPa | 120000 psi | |
| Special Metals INCOLOY® 27-7MO Super-Austenitic Stainless Steel INCOLOY® alloy 27-7MO (UNS S31277; EP 1,263,999 B1) is an advanced 7% molybdenum super-austenitic stainless steel offering corrosion resistance in most environments superior to 6% molybdenum super-.. |
|||