- Polymer Property : Tensile Strength, Ultimate = 16.0 MPa
Polymer Property : Tensile Strength, Ultimate = 16.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| NCMT NanoPAC™ S206 High Performance Polypropylene Nanocomposite Characteristics: High stiffness Supplementary of ABS Good impact resistant Less shrinkage Good thermal conductivity Applications: Toys Industry AutomobileInformation provided by Nano Composite Mater.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| North Wood Plastics HDPE with 40% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Fluorel™ FE-5640Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Fluorel™ FE-5641Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Fluorel™ FC-2180 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Lower mold shrinkage and excellent co.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Fluorel™ FE-5622Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series grades are Dyneon's cle.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Fluorel™ FE-5642Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series grades are Dyneon's cle.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Fluorel™ FC-2123 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Excellent hot tear and compression se.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Fluorel™ FC-2178 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa @Temperature 120 °C |
2320 psi @Temperature 248 °F |
ISO 527 |
| LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| ExxonMobil Escorene® LD-612 EVA Injection Molding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 5.8% vinyl acetate copolymer resin designed for molding and extrusion applications requiring low temperatures, flexibility and toughness. This re.. |
|||
| Tensile Strength, Ultimate | 16.0 - 110 MPa | 2320 - 16000 psi | Average value: 67.9 MPa Grade Count:16 |
| Overview of materials for Polycarbonate, Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Conductive". Each property range of values reported is minimum and maximum values of appr.. |
|||
| Tensile Strength, Ultimate | 16.0 - 4200 MPa | 2320 - 609000 psi | Average value: 74.0 MPa Grade Count:86 |
| Overview of materials for High Density Polyethylene (HDPE), Ultra High Molecular Weight This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Ultra High Molecular Weight". Each property range of values reported i.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| ITW Plexus Plexusâ„¢ 3940 Methacrylate Adhesive An adhesive with versatile substrate and application capabilities for a wide range of industrial product assembly applications.Fast tacking, low pressure sprayable adhesive with long bonding range, .. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| Freudenberg Simrit Simriz® 482 Low Temperature FFKT Perfluoroelastomer Compound Perfluoro elastomers – or FFKM for short – have an ideal combination of characteristics, with their excellent chemical resistance, high level of temperature resistance, and high levels of .. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 301 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638/D412 |
| Covestro Bayflex® 110 RIM-LITE Polyurethane Elastomeric RIM, 13% Mineral Filled, MDI-based 2-Component Liquid System Contains 10% calcium silicate and 3% glass microspheres.0.15 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, .. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | Die C (35 min / 145°C); ASTM D412 |
| Dow SE BR-1220L Stereospecific high cis-1,4 Polybutadiene (BR) SE BR-1220L is manufactured by a solution process using cobalt catalyst which produces polymers with a very light color and low ash content. A non-staining stabilizer is added during the production.. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 342 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| Huntsman PE1403 EVA Film Extrusion
(discontinued **) 4% Vinyl Acetate EVA Copolymer, DMF listed and FDA compliantFeatures: High clarity film with good toughness and flexibility at low temperatures.Applications: Film extrusion: frozen food and general .. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| LyondellBasell Astryn 65F5-4 Polypropylene Homopolymer, 40% Calcium Carbonate Key Features: conventional melt flow, high modulus, mineral-filled polypropylene homopolymer, high stiffness, excellent chemical resistance, good surface qualityApplications: automotive components, .. |
|||
| Tensile Strength, Ultimate | 16.0 - 67.0 MPa | 2320 - 9720 psi | Average value: 42.9 MPa Grade Count:7 |
| Overview of materials for ABS/Polyurethane Alloy This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyurethane Alloy". Each property range of values reported is minimum and maximum values of appropr.. |
|||
| Tensile Strength, Ultimate | 16.0 - 38.0 MPa | 2320 - 5510 psi | Average value: 27.4 MPa Grade Count:11 |
| Overview of materials for Thermoset Polyurethane, Elastomer, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Elastomer, Glass Filled". Each property range of values reported is minimum and .. |
|||
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | |
| 3M Dyneon™ Aflas® FA-150P PTFE Fluoroelastomer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 57%F in polymer with 19% Medium Thermal Carbon Black (N990), 4% Triallyl Isocyanurate (TAIC), 1% Percadox™ 14, 1% Sodium.. |
|||