Polymer Property : Tensile Strength, Ultimate = 19600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	45.0 - 135 MPa @Temperature 60.0 - 150 °C	6530 - 19600 psi @Temperature 140 - 302 °F	Average value: 86.3 MPa Grade Count:2
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Tensile Strength, Ultimate	20.0 - 135 MPa @Temperature -40.0 - 120 °C	2900 - 19600 psi @Temperature -40.0 - 248 °F	Average value: 62.1 MPa Grade Count:7
Overview of materials for Nylon 6, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Mineral Filled". Each property range of values reported is minimum and maximum values of ap..
Tensile Strength, Ultimate	55.0 - 135 MPa	7980 - 19600 psi	Average value: 104 MPa Grade Count:15
Overview of materials for Nylon 66/6, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are incl..
Tensile Strength, Ultimate	10.0 - 135 MPa @Temperature 60.0 - 150 °C	1450 - 19600 psi @Temperature 140 - 302 °F	Average value: 68.8 MPa Grade Count:4
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M..
Tensile Strength, Ultimate	10.0 - 135 MPa @Temperature 60.0 - 150 °C	1450 - 19600 psi @Temperature 140 - 302 °F	Average value: 70.2 MPa Grade Count:2
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% ..