Polymer Property : Tensile Strength, Ultimate = 27.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ASTM D638-61T
Rotuba 856, Slow Burning Ethyl Cellulose Data provided by the manufacturer.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	4.0 mm thick, 10.0 mm wide molded rod; ISO 527
Premix Thermoplastics PRE-ELEC® ESD 7100 PRE-ELEC ESD 7100 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7100 has been developed for inject..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ASTM D638
Rotuba MSS Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer.
Tensile Strength, Ultimate	27.0 - 156 MPa	3920 - 22600 psi	Average value: 87.9 MPa Grade Count:87
Overview of materials for Polycarbonate/ABS Alloy, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Glass Fiber Filled". Each property range of values reported is minimum and maxi..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ASTM D638
Solvay Specialty Polymers Algoflon® 15GL+3Mos PTFE; Glass Fiber/Molybdenum Disulphide Filled (discontinued ** Data provided by the manufacturer.15 wt.% Glass Fiber + 3 wt.% MoS2. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric pro..
Tensile Strength, Ultimate	27.0 - 33.0 MPa	3920 - 4790 psi	Average value: 29.0 MPa Grade Count:3
Overview of materials for Nylon 612, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Impact Modified". Each property range of values reported is minimum and maximum values of app..
Tensile Strength, Ultimate	27.0 MPa	3920 psi
Freudenberg Simrit Superiorâ„¢ F850 Fluoroelastomer Cost-effective, high performance compound for semiconductor applications. Superior F850 offers outstanding plasma resistance and low particulation in a wide range of plasma environments.
Tensile Strength, Ultimate	27.0 MPa @Temperature 22.0 Â°C	3920 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® BMC 0410 Unsaturated Polyester UP BMC 0410 is a low profile BMC with zero shrinkage and low coefficient of thermal expansion. It is especially suited for precision mouldings in office and communication equipment. The combination of ..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ASTM D638
LyondellBasell Hifaxâ„¢ ETA-3131EUV Thermoplastic Olefin Resin Key Features: fractional melt flow, medium modulus, UV-stabilized, extrusion grade thermoplastic olefin resin, excellent impact and stiffness balance, good practical impact, good processability, exc..
Tensile Strength, Ultimate	27.0 MPa	3910 psi
Shinil Chemical SHINNANO PP Polymer Nanocomposite Door Trim SHINNANO is the product line of polymer nanocomposite made by dispersing nano fillers, mainly, NANOCLAY. Recently, Shinil has developed varios nanocomposite grades for automotive applications using..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ISO 527-1, 2
Polyplastics Duracon® TD-35 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ISO 527-1
Chengdu Polyster H4543 Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and injection grade. Contains improved color- stable antioxidants. Applications requiring high original color retention. Molded and injected products for consumer use, such as se..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ISO 527
Eastman Eastar GN071 Natural PETG Copolyester EASTAR GN071 Copolyester is used for injection molding applications. It is sparkling clear, tough, chemical resistant, odor free, versatile, easy to work with and affordable. Cleaning solutions wi..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ASTM D638
A. Schulman ComAlloy Voloy® 100 Polypropylene, Mineral Reinforced, Flame Retardant, UL, CSA Data provided by the manufacturer, ComAlloy International Company.15% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	27.0 - 35.0 MPa	3920 - 5080 psi	ISO 527
BASF Ecovio® C2224 F Blend Biodegradable Polyester Description: Ecovio® F Blend C2224 is our biodegradable film product containing renewable resources. It is basically a compound of our biodegradable copolyester Ecoflex® F Blend and polylactic aci..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ASTM D638
Toyobo E3070A Thermoplastic Polyurethane Elastomer, Extrusion Grade Polyether type, featuring excellent resistance to hot water and fungus. Various grades of Toyobo polyurethane TPEs are used in auto parts, hoses, tubes, sporting goods, shoe soles, etc.Information ..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	at max load; ASTM D638
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman.
Tensile Strength, Ultimate	27.0 - 63.0 MPa	3920 - 9140 psi	Average value: 39.5 MPa Grade Count:20
Overview of materials for Acetal Copolymer, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Impact Modified". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate	27.0 MPa	3920 psi	ASTM D412
KKPC KOSYN KTR 601 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR101 is linear block copolymer made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is thermoplastics ..
Tensile Strength, Ultimate	<= 27.0 MPa	<= 3920 psi	With carbon black or gum stocks. ASTM D412-80
DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, General Description (disc Product form is white, odorless chips. Distinguishing Feature: High viscosity polymer. Good low temperature and heat resistance. Good processing at high extensions.27 % Chlorine Content. 1% Sulf..