Premix Thermoplastics PRE-ELEC® ESD 7100

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® ESD 7100.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC ESD 7100 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7100 has been developed for injection molding and for the extrusion of thermoformable mono- or multi-layer sheet. The products made out of PRE-ELEC ESD 7100 are washable, reusable and recyclable. Surface resistance values of 108 ohms (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters.Typical applications include trays, tote bins, crates and technical parts which give permanent ESD protection for the electronics, medical, pharmaceutical and paper handling industries. PRE-ELEC ESD 7100 can be colored into various bright colors.Information provided by Premix Thermoplastics Inc.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
4 mm thick;10.0 mm wide molded rod; ISO 294-4
Melt Flow 5.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
5.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
High Load Melt Index 20 g/10 min

@Load 21.6 kg,
Temperature 200 °C
20 g/10 min

@Load 47.6 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 73

@Thickness 1.00 mm
73

@Thickness 0.0394 in
sheet; ISO 868
Tensile Strength, Ultimate 27.0 MPa
3920 psi
4.0 mm thick, 10.0 mm wide molded rod; ISO 527
Tensile Strength, Yield 35.0 MPa
5080 psi
4.0 mm thick, 10.0 mm wide molded rod; ISO 527
Elongation at Break 28 %
28 %
4.0 mm thick, 10.0 mm wide molded rod; ISO 527
Elongation at Yield 6.0 %
6.0 %
4.0 mm thick, 10.0 mm wide molded rod; ISO 527
Modulus of Elasticity 1.80 GPa
261 ksi
4 mm thick;10.0 mm wide molded rod; ISO 178
Izod Impact, Notched 1.10 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
2.06 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf
Vicat Softening Point 88.0 °C
190 °F
Rate A; 4 mm thick;10.0 mm wide molded rod; ISO 306/A50
Electrical Properties Metric English Comments
Surface Resistance <= 1.00e+10 ohm

@Thickness 1.00 mm
<= 1.00e+10 ohm

@Thickness 0.0394 in
sheet; ISO IEC 61340-5-1
Static Decay <= 2.0 sec

@Thickness 1.00 mm
<= 2.0 sec

@Thickness 0.0394 in
sheet; ISO IEC 61340-5-1
Processing Properties Metric English Comments
Middle Barrel Temperature 180 °C
356 °F
Zone 1; Cylinder
190 °C
374 °F
Zone 2; Cylinder
200 °C
392 °F
Zone 3; Cylinder
200 °C
392 °F
Zone 6; Cylinder
200 °C
392 °F
Zone 4; Cylinder
200 °C
392 °F
Zone 5; Cylinder
Die Temperature 188 °C
370 °F
Zone 3
199 °C
390 °F
Zone 4
199 °C
390 °F
Zone 1
199 °C
390 °F
Zone 5
199 °C
390 °F
Zone 2
Melt Temperature 190 - 210 °C
374 - 410 °F
Mold Temperature 30.0 - 70.0 °C
86.0 - 158 °F
Roll Temperature 50.0 °C
122 °F
3rd Roll
60.0 °C
140 °F
2nd Roll
60.0 °C
140 °F
1st Roll
Drying Temperature 70.0 - 80.0 °C

@Time 10800 - 14400 sec
158 - 176 °F

@Time 3.00 - 4.00 hour
Pre-drying in a dehumidifier
Moisture Content <= 0.15 %
<= 0.15 %
When Produced
Injection Pressure 75.2 - 120 MPa
10900 - 17400 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Appearance Granule
Color Whitish
Injection Speed Moderate
Post Pressure, psi 5800 - 8700