Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | X, Y direction; ASTM D638 |
Rogers Corporation RT/duroid® 6202 High Frequency Laminate Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | X, Y direction; ASTM D638 |
Rogers Corporation RT/duroid® 6202PR High Frequency Laminate Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527-2 |
NOVA Chemicals DYLARK® 378 Impact Grade Engineering Resin Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | |
Chevron Phillips 7108T LLDPE Sheeting Resin
(discontinued **) Resin Type: Sheeting Resin for the Geomembrane Market; ASTM D 4976 Classification: PE 214, A 35307Applications:Cast Geomembrane Applications, Sanitary Landfill Liners, Waste Water Reservoir Containm.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527 |
LATI LASTIROL TR-V0 Polystyrene (PS) (UL94 V-0)
(discontinued **) Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass f.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | DIN 53455 |
Ineos Nova S-4400 High Impact Compact Polystyrene
(discontinued **) Impact polystyrene which combines excellent flow characteristics with a good dimensional stability under heat and a high stiffness. This grade is designed for injection molding of technical parts o.. |
|||
Tensile Strength, Ultimate | 30.0 - 45.0 MPa @Temperature 60.0 - 90.0 °C |
4350 - 6530 psi @Temperature 140 - 194 °F |
Average value: 37.5 MPa Grade Count:1 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Carbon Fiber Filled". Specific grades with carbon fiber conte.. |
|||
Tensile Strength, Ultimate | 30.0 - 44.9 MPa | 4350 - 6510 psi | Average value: 41.3 MPa Grade Count:11 |
Overview of materials for PVC, High Impact This property data is a summary of similar materials in the MatWeb database for the category "PVC, High Impact". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Ultimate | 30.0 - 62.0 MPa | 4350 - 8990 psi | Average value: 48.7 MPa Grade Count:21 |
Overview of materials for Phenolic, Novolac, Impact Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Impact Grade, Filled". Each property range of values reported is minimum and maximum .. |
|||
Tensile Strength, Ultimate | 30.0 - 147 MPa | 4350 - 21300 psi | Average value: 73.2 MPa Grade Count:90 |
Overview of materials for Nylon 6, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Bead Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
Tensile Strength, Ultimate | 30.0 - 128 MPa | 4350 - 18500 psi | Average value: 68.4 MPa Grade Count:58 |
Overview of materials for Nylon 6, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ.. |
|||
Tensile Strength, Ultimate | 30.0 - 215 MPa | 4350 - 31200 psi | Average value: 149 MPa Grade Count:581 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 30.0 - 299 MPa | 4350 - 43400 psi | Average value: 219 MPa Grade Count:91 |
Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Tensile Strength, Ultimate | 30.0 MPa @Temperature 1205 °C |
4350 psi @Temperature 2201 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Ultimate | 30.0 MPa @Temperature 22.0 °C |
4350 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® BMC 2910 Unsaturated Polyester UP BMC 2910 incorporates additives which enhance the integral performance of mouldings during and after fire, currently used to mould Boltcaps which are designed to provide protection to the bolted co.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527-1 |
Chengdu Polyster H5550B Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and extrusion grade. Contains color-stable antioxidants. Good balance of low and high temperature properties. Excellent flex-fatigue resistance. Excellent creep resistance. CVJ b.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527-1 |
Dow BETAMATE™ 1045 Epoxy BETAMATE™ 1045 is a one component, epoxy based adhesive especially developed for the body shop. The product has the following properties: Good rheology performance (Wash-out resistant, excellent.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ASTM D638 |
Eastman Eastar GN071 Natural PETG Copolyester EASTAR GN071 Copolyester is used for injection molding applications. It is sparkling clear, tough, chemical resistant, odor free, versatile, easy to work with and affordable. Cleaning solutions wi.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO R527 |
Arkema Group Orgalloy® LT 4060 ES Polyamide Alloy Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
Alliance BIF-17 Bonded (Composite) Magnetic Material |
|||
Tensile Strength, Ultimate | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
Alliance BIF-2 Bonded (Composite) Magnetic Material |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 110 Polypropylene, Mineral Reinforced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.15% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 30.0 MPa @Temperature 899 °C |
4350 psi @Temperature 1650 °F |
0.059" Coil |
AK Steel 15 Cr-Cb® ULTRA FORM® Ferritic Stainless steel AK Steel’s 15 Cr-Cb ULTRA FORM® is a low-carbon, low-nitrogen ferritic grade of stainless steel with an intermediate, 14.5% chromium content. Alloying additions of Ti, Cb, Si and Mn provide excell.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 37 |
Lubrizol ESTANE® 58141 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 30.0 - 35.9 MPa | 4350 - 5210 psi | Average value: 33.9 MPa Grade Count:3 |
Overview of materials for Polypropylene, Sheet/Thermoforming Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Sheet/Thermoforming Grade". Each property range of values reported is minimum and maximum.. |
|||
Tensile Strength, Ultimate | 30.0 - 150 MPa | 4350 - 21800 psi | Average value: 96.4 MPa Grade Count:97 |
Overview of materials for Polypropylene with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Glass Fiber Filler". Specific grades with glass content between 35% and 44% are i.. |