- Polymer Property : Tensile Strength, Ultimate = 5950 psi
Polymer Property : Tensile Strength, Ultimate = 5950 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | 5 mm/min |
| Polimeri Europa EDISTIR N1460 Polystyrene
(discontinued **) Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,E,085-03 High molecular weight general purpose polystyrene with good mechanical strength. This grade is especially recomme.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | 5 mm/min |
| Polimeri Europa EDISTIR N1461 Polystyrene
(discontinued **) Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,M,085-03 High molecular weight general purpose polystyrene with good mechanical strength. Well suitable for injection mold.. |
|||
| Tensile Strength, Ultimate | 41.0 - 70.0 MPa | 5950 - 10200 psi | Average value: 55.1 MPa Grade Count:10 |
| Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled". Each property range of values report.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa @Temperature 60.0 °C |
5950 psi @Temperature 140 °F |
ISO 527 |
| LATI LATILUB 73/13-01M Polyoxymethylene Base (POM), 1% Molybdenum Disulfide Self Lubricating Plastic
(Unv Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
| Tensile Strength, Ultimate | 41.0 - 107 MPa | 5950 - 15500 psi | Average value: 77.7 MPa Grade Count:13 |
| Overview of materials for Epoxy, Encapsulating, Glass or Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Glass or Mineral Filled". Each property range of values reported is minimum and ma.. |
|||
| Tensile Strength, Ultimate | 41.0 - 60.5 MPa | 5950 - 8770 psi | Average value: 50.5 MPa Grade Count:12 |
| Overview of materials for Phenolic, Novolac, Heat Resistant Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Heat Resistant Grade, Filled". Each property range of values reported is minimum and .. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| IDI Composites 44-10 Thermoset Polyester, Molding Multi-purpose medium strength material with excellent surface appearance, corrosion resistance, and V-O flame resistance.Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| IDI Composites 48-50 Thermoset Polyester, Molding Moderate strength electrical grade with good track resistance and V-O flame resistance.Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| IDI Composites C-103 Thermoset Polyester, Molding Vinylester compounds in a range of strengths with superior corrosion resistance.Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 MPa @Temperature 1149.0 °C |
5950 psi @Temperature 2100.2 °F |
|
| Haynes HR-160® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Tensile Strength, Ultimate | 41.0 - 55.0 MPa | 5950 - 7980 psi | |
| Cosmic Plastics 6130F Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Cosmic Plastics K31 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | |
| Cosmic Plastics K43 Mineral Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Cosmic Plastics K77 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Plenco 6343 Phenolic, Granular, Transfer Molded PLENCO 06343 is a mica reinforced phenolic molding compound, offering for a low power factor, low electrical losses, and good electrical properties after long exposures to high humidity. UL recogniz.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa @Thickness 2.00 mm |
5950 psi @Thickness 0.0787 in |
molded plaque, cured 20 hr at 100°C; ASTM D412 |
| BASF Elastollan® 1175A10W Wire & Cable Grade Polyurethane Elastomer As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D412 |
| BASF Elastollan® S74D Polyester Type Polyurethane Elastomer Recommended for injection molding. Elastollan S series of products are polyester-based thermoplastic polyurethanes that exhibit good hydrolytic stability. They also exhibit good oil, fuel and solv.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ATSM D638 |
| Ashley Polymers Ashlene® 527LDMS Nylon 66 A very high impact Nylon 66 with Molybdenum disulfide designed to combine high impact with a reduced co-efficient of friction.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ATSM D638 |
| Ashley Polymers Ashlene® 940H Nylon 11 A general purpose highly flexible natural Nylon 11 resin with UV stabilizers.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D412 |
| BASF Elastollan® 1164D Polyether Type Polyurethane Elastomer Recommended for injection molding. Elastollan ® 1100 series products are FDA Sec. 177.2600 compliant. Elastollan 1100 series of products are polyether-based thermoplastic polyurethanes. They exhi.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D412 |
| BASF Elastollan® C-90A Polyester Type Polyurethane Elastomer Processed by extrusion or injection molding. Elastollan C series of products are polyester-based thermoplastic polyurethanes that exhibit very good hydrolytic stability. They also exhibit excellen.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D651 |
| Resinoid 2010 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Cosmic Plastics 6120F Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 - 55.2 MPa | 5950 - 8010 psi | Average value: 49.6 MPa Grade Count:12 |
| Overview of materials for Diallyl Phthalate (DAP), Cast, Mineral Filler This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP), Cast, Mineral Filler". Each property range of values reported is minimum and ma.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Kleerdex Kydex® 1900 Acrylic/PVC Thermoplastic Sheet
(discontinued **) Mid-temperature aircraft gradeApplications: This sheet product is designed for use in small aircraft interiors but also is appropriate for other applications where higher in-service temperatures may.. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Plaslok 302 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 302 is a two-stage, woodflour and flo.. |
|||
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Cosmic Plastics 6120 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | |
| Cosmic Plastics 6160 Mineral Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 - 55.0 MPa | 5950 - 7980 psi | |
| Cosmic Plastics 6230F Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Cosmic Plastics D33 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||