Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 11.0 - 17.2 MPa | 1600 - 2500 psi | |
ND Industries High Temperature SuperGlue 362 Medium viscosity with thermal cycling resistance |
|||
Shear Strength | 11.0 MPa @Temperature 65.6 °C, Time 7200 sec |
1600 psi @Temperature 150 °F, Time 2.00 hour |
Lap |
Parker Chomerics CHO-BOND 360-20 Conductive Epoxy Low cost, electrically conductive epoxy adhesive that combines the good adhesive characteristics as epoxy, and the superior electrical conductivity of silver. It is recommended as a thermo-setting E.. |
|||
Shear Strength | 11.0 MPa | 1600 psi | Cured 30 minutes at 150°C, Al/Al |
Resin Technology Group TIGA 908 Gold Bonder - Low Stress Silver Conductive 100 parts resin to 6 parts hardener.TIGA 908 is a low stress, conductive silver filled epoxy adhesive. It is recommended for bonding, and sealing electronic applications which require bonding to gol.. |
|||
Shear Strength | 11.0 - 164.095 MPa @Temperature -55.0 - 177 °C |
1600 - 23800.0 psi @Temperature -67.0 - 351 °F |
Average value: 58.8 MPa Grade Count:26 |
Overview of materials for Epoxy Cure Resin This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Cure Resin". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Shear Strength | 11.0 MPa | 1600 psi | Shear Bond Holding Strength |
Indium Corp. Indalloy® 3 In-Ag Solder Alloy Has nearly the wettability and low temperature malleability of Indium. Solders silver, fired glass, and ceramics. Large plastic range.Information provided by the manufacturer, Indium Corporation. |
|||
Shear Strength | 11.0 - 13.8 MPa | 1600 - 2000 psi | |
ITW Plexus Plexusâ„¢ MA590 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose, long open time product and bond lines up to 1" thickInformation provided by Illinois .. |
|||
Shear Strength | 11.0 MPa | 1600 psi | |
Sawbones Solid Rigid Polyurethane Foam 40 pcf Density Solid Rigid Polyurethane FoamPrimary UseSolid rigid polyurethane foam is primarily used as an alternative test medium for human cancellous bone. These products are not intended to replicate the mech.. |
|||
Shear Strength | 11.0 MPa | 1600 psi | Bond, Al to Al, RT cure |
Master Bond Supreme 11AO Electrically Isolating Adhesive and Sealant Description: Master Bond Polymer System SURPEME 11AO is a two component epoxy resin system for high performance bonding and sealing formulated to cure at room temperature or more rapidly at elevated.. |
|||
Shear Strength | 11.0 MPa | 1600 psi | Overlap, Fiberglass |
3M Scotch-Weld™ DP190 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information pro.. |
|||
Shear Strength | 11.0 MPa @Temperature -29.0 °C |
1600 psi @Temperature -20.2 °F |
Overlap, Adhesion Failure |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 11.0 MPa | 1600 psi | Overlap, Wood (Fir) (dry wipe)-Substrate Failure; ASTM D1002 |
3M Scotch-Weld™ LSB90 Flexible Epoxy 3M™ Scotch-Weld™ Epoxy Adhesive LSB90 is a high performance, two-part, flexible epoxy adhesive offering high shear and peel adhesion and very high levels of durability. It has a 90 minute worklife.. |
|||
Shear Strength | 11.0 MPa | 1600 psi | Overlap, FR-4/FR-4 tested after 90°C/2 wks/90% RH |
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |