Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.90 GPa @Temperature 23.0 °C |
276 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PP CQX30030 RTX Polypropylene, Mineral Reinforced, Scratch Resistant Information provided by Polykemi AB |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics GELOY FXW710SK ASA General purpose injection molding ASA with Visual Fx sparkle effect. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178, ASTM D790 |
Nilit Nilamid A3 H ZC High Impact PA66 Description: Nilamid A3 H ZC has outstanding impact performance, even at minus temperatures. It is widely used for components subjected to high shock loads. Applications include bicycle components, .. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | DIN 53452; ASTM D790 |
Kolon Kopa® KN161 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
Inno-Comp INNOPOL® CS 3-3120 B 20% Talc-Filled Polypropylene INNOPOL® CS 3-3120 B is a black colored, 20% talc-filled polypropylene compound.INNOPOL® CS 3-3120 B is a recommended for producing injection molded products where the required property is hig.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | Tangent, 0.05 in/min; ASTM D790 |
LyondellBasell Hostacomâ„¢ 62F4-2C Polypropylene Homopolymer Description: Hostacomâ„¢ 62F4-2C high melt flow, 1,900 MPa flexural modulus, precolored, 20% talc-filled polypropylene homopolymer has excellent heat aging characteristics, high chemical resistan.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
LyondellBasell Hostacomâ„¢ CB280F Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB280F high melt flow, 1,900 MPa flexural modulus, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of processability, .. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® CL402 PBT+PC (Asia Pacific) XENOY CL402 is a high viscosity, unfilled, elastomer modified PC/PBT blend for extrusion/blowmolding applications. ISO1043-label: PC+PBT-I.This data was supplied by SABIC-IP for the Asia Pacific reg.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC (Asia Pacific) Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC (Europe-Africa-Middle East) Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Europe-Africa-Middle East) PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent |
|||
Flexural Modulus | 1.90 GPa @Thickness 3.20 mm |
276 ksi @Thickness 0.126 in |
3-points, 2 mm/min, Injection Molded; ISO 178 |
Styron MAGNUMâ„¢ 3904 Smooth Acrylonitrile Butadiene Styrene (ABS) Resin Overview: MAGNUMâ„¢ 3904 is an extrusion/thermoforming resin developed for high impact and other technical applications. The mass (continuous process) ABS technology of Styron ensures an ABS tech.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Europe-Africa-Middle East) NORYL GTX944 is an unfilled GTX grade with improved processability and increased impact performance. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® XD1575S PBT+PC (Europe-Africa-Middle East) XENOY XD1575S is a high flow PC+PBT blend with good impact properties and good resistance to occasional solvent and gasoline contact. XENOY XD1575S has been specially developed for coated exterior b.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
SABIC Innovative Plastics NORYL ECN0240 PPE+PS (Asia Pacific) PPE+PS, Auto exterior grade |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 2mm/min; ISO 178 |
Borealis Daplen™ EE188HP Polypropylene TPO Compound Daplen™ EE188HP is a 15% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and g.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
Total PS CPDS 863 High Flow Flame Retardant Deca Polystyrene Total Petrochemicals Polystyrene 863 is a high flow, heat resistant, high impact polystyrene for injection molding. It is recommended for the manufacturing of articles which require good dimensiona.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1603 Glass Reinforced Copolymer DescriptionPolyfort® FPP 1603 is a 10% glass reinforced copolymer. It has good impact and heat resistance. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
Eastman DURASTAR DS2010 Natural PCTA Copolyester DURASTAR DS2010 polymer contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing cha.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
Cossa Polimeri ESTABLEND PA 6000 ABS / Nylon 6 Blend ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.Easy processing, high surface quality, high chemical resistance, good heat resistanceInformation provided by Cossa Polimeri.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D 790 |
Cossa Polimeri ESTAPROP 1040 V2 K Flame Retardant Polypropylene PP copolymerFlame retardant class V2, halogen free, good mechanical characteristicsInformation provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D 790 |
Cossa Polimeri ESTASTIR HI 0412 Polystyrene Polystyrene for injection molding or extrusionHigh impact resistance, good thermal resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600/58 HWCP Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | 2mm/min; ISO 178 |
Denka MALECCA K-700 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ISO Data |
BASF Ultramid® 8253 PA6 (Dry) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
Ashley Polymers Ashlene® 981S Nylon 612 A general purpose heat stabilized 612 Nylon for extrusion. These resins are noted for their low moisture absorption and excellent dimensional stability.Data provided by the manufacturer |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
Total Lacqrene® 4801
(discontinued **) LACQRENE® 4801 is an easy flowing, high impact polystyrene for injection molding. The very good processing characteristics of this grade allows for the production of thin articles with long flow p.. |
|||
Flexural Modulus | 1.90 - 9.65 GPa | 276 - 1400 ksi | Average value: 4.72 GPa Grade Count:26 |
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and.. |
|||
Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
Adell RA-16 Copolymer Polypropylene, 30% Talc Filled Data provided by Adell Plastics, Inc. |