Polymer Property : Flexural Modulus = 1.58 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.58 GPa	229 ksi	Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790
Network Polymers MS 175 Styrene Methyl Methacrylate Terpolymer Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc.
Flexural Modulus	1.58 - 3.53 GPa	229 - 512 ksi	Average value: 3.13 GPa Grade Count:65
Overview of materials for Polystyrene, Transparent Grade This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Transparent Grade". Each property range of values reported is minimum and maximum values of..
Flexural Modulus	1.58 GPa @Temperature 23.0 Â°C	229 ksi @Temperature 73.4 Â°F	ASTM D790A
Ineos H38G-02 Polypropylene Homopolymer This is a polypropylene homopolymer for general purpose injection molding and high speed spinning applications. It is useful for spun bonded nonwovens and partially oriented yarn (POY). This mater..
Flexural Modulus	1.58 GPa	229 ksi	2 mm/min; ISO 178
Inno-Comp INNOPOLÂ® CS 2-9000 MA N Polypropylene Copolymer INNOPOLÂ® CS 2-9000 MA N is a high melt flow copolymer with antistatic additive.INNOPOLÂ® CS 2-9000 MA N is developed for producing injection molded automotive components.All information provide..
Flexural Modulus	1.58 GPa	229 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant.
Flexural Modulus	1.58 GPa	229 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-LOY A3000TXJ ABS LNP* STAT-LOY* A3000TXJ is a product based on ABS resin. Added features of this material include: Antistatic, Transparent, Formulated with FDA Food Contact Additives.
Flexural Modulus	1.58 GPa	229 ksi	2.8 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VE-0855YS ABS, Unreinforced FR Flame-retardant ABS that can be used in the exterior of monitorsInformation provided by Samsung Cheil Industries.
Flexural Modulus	1.58 GPa	229 ksi	2.8 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® VE-0855YS ABS, Unreinforced FR Flame-retardant ABS that can be used in the exterior of monitorsInformation provided by Samsung Cheil Industries.
Flexural Modulus	1.58 GPa	229 ksi	ASTM D790
Braskem H 201 Fiber Extrusion Polypropylene Applications: Staple fibers for carpets and blankets; continuous filament for ropes, cords and rugs. Information provided by Braskem
Flexural Modulus	1.58 GPa	229 ksi
Abatron AboCast 50-11/AboCure 50-1 Epoxy Information provided by Abatron, Inc.Processing: Shelf life: 12+ months (unmixed). 100/35 ratio. Pot life: 500 g, 240 min. at 25°C(77°F). Exothermic Peak 190°C (375°F). Hardens in 2-24 hours..
Flexural Modulus	1.58 - 3.16 GPa	229 - 458 ksi	Average value: 2.44 GPa Grade Count:11
Overview of materials for Styrene/Methyl Methacrylate Copolymer (SMMA) This property data is a summary of similar materials in the MatWeb database for the category "Styrene/Methyl Methacrylate Copolymer (SMMA)". Each property range of values reported is minimum and max..