Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.60 GPa @Temperature 23.0 °C |
232 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPC T4020 E20 Polypropylene Copolymer, Mineral Reinforced, Modified Information provided by Polykemi AB |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
Inno-Comp INNOPOL® CS 2-3120 TO 20% Talc Filled Polypropylene Block-Copolymer INNOPOL® CS 2-3120 TO is a 20% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-3120 TO is developed for pro.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 1% Secant; ASTM D790 |
IRPC Polimaxx Polene 1202J Polypropylene Homopolymer CHARACTERISTICS: GOOD STIFFNESS, GOOD EXTRUDABILITY, HIGH IMPACTAPPLICATIONS: MONOFILAMENT/YARN/SHEET EXTRUSION AND INJECTION MOLDING COARSE TEXTILE FOR JUMBO BAGS, ROPES, STRAWS, SHEETS, INDUSTRIAL.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
LyondellBasell Hostacomâ„¢ BG751P Polypropylene Description: Hostacomâ„¢ BG751P very high melt flow, 1,600 MPa flexural modulus, UV-stabilized, natural, 20% calcium carbonate-filled, modified polypropylene resin has a unique balance of process.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
LyondellBasell Hostacomâ„¢ TKS709D Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ TKS709D medium high melt flow, 1,600 MPa flexural modulus, UV-stabilized, thermoplastic elastomeric olefin (TEO) resin has an excellent combination of properties and proc.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP ML008 PP (Europe-Africa-Middle East) LNP* LUBRICOMP* ML008 is a compound based on Polypropylene resin containing PTFE. Added Features include: Internally Lubricated. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON MD000I PP (Europe-Africa-Middle East) LNP* Stat-kon* MD000I is a compound based on Polypropylene resin. Added features of this material include: Electrically Conductive, High Impact. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
Suzhou Hipro Polymers Hiprolon® 200 NN Nylon 1010, dry Hiprolon® 200 NN is a medium viscosity polyamide 10,10 with neat resin based on bio-renewable resource. It features low density, low water absorption, good cold impact resistance, good wear-resi.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene DescriptionPolyfort® FXP 3000-3120 is a 30% glass sphere filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM-D790 |
Polyram PlusTek PB891 Nylon 6, Impact Modified Impact modified polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Tipco Tipcolene® FPT 10 PPC - 10% Talc Reinforced Polypropylene Copolymer Compound 10% Talc Reinforced PP CopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178-93 |
Wellman Wellamid® XT1482-BK High Impact Nylon 66 Description: High Impact Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | Tangent; ASTM D790 |
Washington Penn PPC3MF1.5-Black Polypropylene, 15% Mica-Filled, Chemically-Coupled Heat Stabilized injection molding compound. Meets physical requirements for General Motors Spec. GMP.PP.024.Applications: HVAC duct and other various automotive applications.Data provided by Washin.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Goodfellow TPX® DX845 Extrusion Grade Polymethylpentene This grade is highly recommended for film extrusion; also for injection molding, fiber extrusion and blow molding.TPX® is semi-crystalline, transparent, very light and - for a polyolefin - expensiv.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | dry; ISO 178 |
DSM Novamid® 1015G50 NA/BK37 PA6-GF50 50% Glass Reinforced, Injection Molding |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | cond; ISO 178 |
DSM Novamid® 3010N 5-SL4-3X NAT PA66 FR Low Viscosity, Molding Release, 30% Glass Reinforced |
|||
Flexural Modulus | 1.60 GPa @Temperature -40.0 °C |
232 ksi @Temperature -40.0 °F |
ASTM D790 |
Arkema Group PLATAMID® 8020 Copolyamide Platamid® 8020 is a transparent, thermoplastic copolyamide designed for conversion by standard molding or extrusion techniques.Information provided by Arkema Group |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | SAE J949 |
Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0334C10L1 Calcium Reinforced |
|||
Flexural Modulus | 1.60 GPa @Temperature 23.0 °C |
232 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PP TOUCH 34725 Polypropylene, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Shell Carilon® D26HM100 Polyketone, General-Purpose Injection Molding Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer D26HM100 is a general-purpose injection molding grade with mechanical properties which classify it .. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Adell RZ-18 Copolymer Polypropylene, 40% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 1.60 GPa @Temperature 23.0 °C |
232 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPHC K8040G E10 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene DescriptionPolyfort® FXP 3000-3120 is a 30% glass sphere filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene DescriptionPolyfort® FXP 3000-3120 is a 30% glass sphere filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Modulus | 1.60 - 8.34266 GPa @Temperature -40.0 - 121 °C |
232 - 1210.02 ksi @Temperature -40.0 - 250 °F |
Average value: 4.93 GPa Grade Count:25 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
Sax Polymers SAXALEN PPH329B20 Polypropylene Homopolymer, 20% Glass Filled SAXALEN PPH329B20 is a 20% glass beads filled Polypropylene - Homopolymer intended for injection molding. Low shrinkage, low warpage gradeInformation provided by SAX Polymers |
|||
Flexural Modulus | 1.60 - 24.8 GPa | 232 - 3600 ksi | Average value: 8.41 GPa Grade Count:56 |
Overview of materials for Polytrimethylene Terephthalate (PTT) This property data is a summary of similar materials in the MatWeb database for the category "Polytrimethylene Terephthalate (PTT)". Each property range of values reported is minimum and maximum val.. |