Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 14.0 - 16.0 GPa | 2030 - 2320 ksi | Injection and Compression; ISO 178 |
Raschig Group 3505 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. This product meets the allowed.. |
|||
Flexural Modulus | 14.0 - 16.0 GPa | 2030 - 2320 ksi | Injection and Compression; ISO 178 |
Raschig Group 3535 Epoxy Glass fiber-reinforced epoxy molding compound. Good mechanical strength, very good electrical isolation properties adn dimensional stability even at high temperatures. Form: Low dust granulate pack.. |
|||
Flexural Modulus | 12.0 - 16.0 GPa | 1740 - 2320 ksi | Injection; ISO 178 |
Raschig Group 4554 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to 300°C, exceptional electrical properties, good mechanical strength, very good dimensional stability. Processi.. |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Compression; ISO 178 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Injection; ISO 178 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Flexural Modulus | 14.0 - 16.0 GPa | 2030 - 2320 ksi | Injection; ISO 178 |
Raschig Group RALUPOL® 8601 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical stren.. |
|||
Flexural Modulus | 14.0 - 16.0 GPa | 2030 - 2320 ksi | Injection; ISO 178 |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Injection; ISO 178 |
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Flexural Modulus | 8.00 - 16.0 GPa | 1160 - 2320 ksi | Average value: 12.5 GPa Grade Count:9 |
Overview of materials for Silicone, Molded, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Silicone, Molded, Glass Fiber Filled". Each property range of values reported is minimum and maximum val.. |
|||
Flexural Modulus | 13.0 - 16.0 GPa | 1890 - 2320 ksi | Injection; ISO 178 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Flexural Modulus | 5.52 - 16.0 GPa | 800 - 2320 ksi | Average value: 9.57 GPa Grade Count:34 |
Overview of materials for Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||
Flexural Modulus | 12.0 - 16.0 GPa | 1740 - 2320 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR N 4203 Bulk Molding Compound Highest dimensional stability under temp. Low profile.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipat.. |