Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.00 - 25.5 GPa @Temperature -40.0 - 250 °C |
725 - 3700 ksi @Temperature -40.0 - 482 °F |
Average value: 13.8 GPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
Flexural Modulus | 5.00 - 25.5 GPa @Thickness 0.790 - 4.00 mm |
725 - 3700 ksi @Thickness 0.0311 - 0.157 in |
Average value: 13.8 GPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
Flexural Modulus | 4.24 - 25.5 GPa | 615 - 3700 ksi | Average value: 12.6 GPa Grade Count:10 |
Overview of materials for Thermoplastic Polyimide, Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyimide, Carbon Fiber". Each property range of values reported is minimum and maximum va.. |
|||
Flexural Modulus | 8.27 - 25.5 GPa | 1200 - 3700 ksi | Average value: 21.1 GPa Grade Count:23 |
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Flexural Modulus | 0.552 - 25.5 GPa | 80.0 - 3700 ksi | Average value: 14.4 GPa Grade Count:18 |
Overview of materials for Polyphenylene Sulfide (PPS), Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Conductive". Each property range of values reported is minimum and maximum .. |