Polymer Property : Flexural Strength = 10900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	75.0 MPa @Temperature 275 °C	10900 psi @Temperature 527 °F	ISO 178
Victrex® PEEK 150GL30 30% Glass Fiber Reinforced Product Description: High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact c..
Flexural Strength	75.0 MPa @Temperature 275 °C	10900 psi @Temperature 527 °F	ISO 178
Victrex® PEEK 90GL30 BLACK EU 30% Glass Fiber Filled, PolyEtherEtherKetone High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding, very easy flow, FDA and EU food contact compliant, ..
Flexural Strength	75.0 MPa @Temperature 275 °C	10900 psi @Temperature 527 °F	ISO 178
Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced Product Description:High performance thermoplastic material, 30% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding, very easy flow, FDA food conta..
Flexural Strength	75.0 MPa @Temperature 275 °C	10900 psi @Temperature 527 °F	ISO 178
Victrex® WG102™ Polyaryletherketone Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliantWG102 does not c..
Flexural Strength	75.0 MPa @Strain 8.00 %	10900 psi @Strain 8.00 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified PA 6, 15% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Strength	75.0 MPa @Strain 8.50 %	10900 psi @Strain 8.50 %	Conditioned; ISO 178
Lanxess DurethanÂ® BKV 215 H3.0 000000 Nylon 6-Copolymer, 15% Glass Fibers PA 6-Copolymer, 15% glass fibers, injection molding, impact modified
Flexural Strength	75.0 MPa @Strain 6.90 %	10900 psi @Strain 6.90 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® DP 1801/30 H3.0 000000 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, halogen free flame retardant.Information provided by LANXESS.
Flexural Strength	75.0 MPa @Temperature 80.0 °C	10900 psi @Temperature 176 °F	Practical Use (Water Absorption 2.1%); ASTM-D790
Toyobo GLAMIDE® T-663G15 Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	75.0 MPa @Temperature 23.0 °C	10900 psi @Temperature 73.4 °F	Practical Use (Water Absorption 2.0%); ASTM-D790
Toyobo GLAMIDE® T-777-02 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	75.0 MPa @Temperature 23.0 °C	10900 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-102ND Nylon/Elastomer GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	75.0 MPa @Temperature 175 °C	10900 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 650GL30 30% Glass Fiber Filled, PolyEtherEtherKetone High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, low flow, color natural/beige.Typical..