Polymer Property : CTE, linear, Parallel to Flow = 13.9 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 50.0 - 150 °C	11.1 - 13.9 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group DECAL® 666/8 Phenolic Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod..
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 50.0 - 150 °C	11.1 - 13.9 µin/in-°F @Temperature 122 - 302 °F	ISO 11359-2
Raschig Group EPOXIDUR® 3581 S ZC EP Epoxy Molding Compound Inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very good sealing connection on ..
CTE, linear, Parallel to Flow	15.0 - 25.0 µm/m-°C @Temperature 50.0 - 100 °C	8.33 - 13.9 µin/in-°F @Temperature 122 - 212 °F	ISO 11359-2
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets..
CTE, linear, Parallel to Flow	15.0 - 25.0 µm/m-°C @Temperature 20.0 °C	8.33 - 13.9 µin/in-°F @Temperature 68.0 °F	TMA
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by ..
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® B3EG5 25% Glass Filled PA6 (Dry) Description: 25% glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating partsInformation provided by BASF
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3EG6 30% Glass Filled PA6 (Dry) Ultramid B3EG6 is a 30% glass fiber reinforced injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500.
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3EG6 BK00564 30% Glass Filled PA6 (Dry) Ultramid B3EG6 BK00564 is a 30% glass fiber reinforced, pigmented black injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500.
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Dry) Information provided by BASF
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3ZG6 30% Glass Filled PA6 (Dry) Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity.
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3ZG6 BK30564 30% Glass Filled PA6 (Dry) Ultramid B3ZG6 BK30564 is an impact-modified, pigmented black, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity.
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el..
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
BASF Ultramid® B3WG5 BK 00654 PA6 25% Glass Filled BK (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el..
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3WG6 30% Glass Filled PA6 (Dry) Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade.
CTE, linear, Parallel to Flow	20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C	11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-1/-2
BASF Ultramid® B3WG6 BK00564 30% Glass Filled PA6 (Dry) Ultramid B3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade.