Thermal Properties | Metric | English | Comments |
---|---|---|---|
Specific Heat Capacity | 0.385 J/g-°C | 0.0920 BTU/lb-°F | |
Weartech International WT-694 Cobalt Hardfacing & Wear Resistant Alloy Information provided by Weartech International |
|||
Specific Heat Capacity | 0.385 J/g-°C @Temperature 20.0 °C |
0.0920 BTU/lb-°F @Temperature 68.0 °F |
|
California Fine Wire Nickel Alloy 180 Copper Nickel Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Specific Heat Capacity | 0.385 J/g-°C @Temperature 20.0 °C |
0.0920 BTU/lb-°F @Temperature 68.0 °F |
|
California Fine Wire Nickel Alloy 30 Copper Nickel Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Specific Heat Capacity | 0.385 J/g-°C @Temperature 20.0 °C |
0.0920 BTU/lb-°F @Temperature 68.0 °F |
|
California Fine Wire Nickel Alloy 60 Copper Nickel Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Specific Heat Capacity | 0.385 J/g-°C @Temperature 20.0 °C |
0.0920 BTU/lb-°F @Temperature 68.0 °F |
|
California Fine Wire Nickel Alloy 90 Copper Nickel Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Specific Heat Capacity | 0.385 J/g-°C | 0.0920 BTU/lb-°F | |
Weartech International WT-25 Cobalt Hardfacing & Wear Resistant Alloy Information provided by Weartech International |
|||
Specific Heat Capacity | 0.385 J/g-°C @Temperature 21.0 °C |
0.0920 BTU/lb-°F @Temperature 69.8 °F |
|
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |