Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Eastar GN125 Copolyester, Natural
(discontinued **) Eastar Copolyester GN125 is a glycol modified polyethylene terephthalate (PET) that contains an ultraviolet light inhibitor. This product is recommended for indoor applications requiring enhanced co.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 |
Eastman 9921P PET Injection Molded
(discontinued **) Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
Eastman Eastapak 9921W PET
(discontinued **) Unreinforced. ISO data as provided by the manufacturer, Eastman Chemical.This product is discontinued; 2003. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75-2 |
Polycasa COPOL PETG QUINN COPOL has good optical properties, brilliant surface, easy to vacuum form without pre-drying, low water absorption, very good chemical resistance, and high impact properties.Bus shelters (UV-v.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
LyondellBasell Lupolen® 3652 D SW 00413 MDPE Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
LyondellBasell Lupolen® 4152 D SW 00413 HDPE Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 |
GEHR Plastics PE-ELS® Polyethylene HDPE A variant of PE-HD with improved electrical conductivity.Polyethylene has a good chemical resistance against almost all acids and bases, detergents and hot water. PE has good insulation properties a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 |
GEHR Plastics PE-HD Polyethylene HDPE Polyethylene has a good chemical resistance against almost all acids and bases, detergents and hot water. PE has good insulation properties and is easy to weld. The operating temperature is from -50.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 68.9 °C | 156 °F | (0.250"); ASTM D648 |
LTL Color Compounds ColorRxâ„¢ PE2-0200RX Biocompatible HDPE A biocompatiblei fractional melt High Density Polyethylene for healthcare applicationsAll information provided by LTL Color Compounders, Inc. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 68.9 °C | 156 °F | (0.250"); ASTM D648 |
LTL Color Compounds ColorRxâ„¢ PE2-0201A Antimicrobial HDPE A fractional melt High Density Polyethylene containing antimicrobial protection. Ingredients are not approved for biocompatibility or food contact applications.All information provided by LTL Color .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 68.9 °C | 156 °F | (0.250"); ASTM D648 |
LTL Color Compounds ColorRxâ„¢ PE2-0202AF Food Grade HDPE A fractional melt High Density Polyethylene containing antimicrobial protection. Ingredients are not approved for biocompatibility or food contact applications.All information provided by LTL Color .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Ineos K46-06-185 HDPE K46-06-185 is a natural high molecular weight, high-density copolymer polyethylene developed for automotive fuel tanks. It combines excellent processability and outstanding physical performance, par.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Lubrizol Estaloc® 61225 Polyester-Type Thermoplastic Alloy Type: Estaloc® 61225 Alloy RETPU is a polyester-type thermoplastic alloy.Features: Fast cycling, dimensional stability, durability, aesthetics, low temperature impact.Uses: Injection molding.Availa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Aspira EN177 Copolyester Resin for Extrusion Blow Molding Applications:Beverage packagingConsumer packagingFood packagingPersonal care packagingKey Attributes:BPA-freeCompatible with high-output manufacturing platformsExcellent clarityHigh gloss appearance.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Cadence™ GS3 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Eastar EN010 Copolyester Eastar copolyester EN010 is used primarily in molded thick wall European applications.Applications/UsesPackagingInjection moldingContainers |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Eastar EN076 Copolyester Eastar Copolyester EN076 is recommended for the thick-walled containers that are prevalent in the cosmetics and personal care markets. This copolyester offers good processability with the benefits o.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
Eastman Eastar GN007 PETG Copolyester ISO data as provided by the manufacturer, Eastman Chemical |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Eastar MN058 Copolyester Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN058 Copolyester is a medical gra.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Eastar MN059 Copolyester Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN059 Copolyester is a medical gra.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman Tenite Acetate 105E1R26029 Clear, Trsp Cellulose Acetate TENITE cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of TENITE cellulosi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 68.9 °C | 156 °F | ISO 75-2/B |
ExxonMobil Exxtral™ BNU 013 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin characterized by a good impact resistance, high stiffness, good scratch and good surface finishing designed for automotive interior ap.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 68.9 °C | 156 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
Dow DMDA-8965 NT 7 High Density Polyethylene Resin DOW DMDA-8965 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM-D648 |
Braskem GD5150K HDPE High Density Extrusion Polyethylene GD5150K is a high-density polyethylene specially developed for the manufacturing of insulation for wires and cables demanding high extrusion velocity. It has medium molar mass, shows good dielectric.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM-D648 |
Braskem GM5010T2B HDPE High Density Extrusion Polyethylene GM5010T2B is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for water distribution. It is produced with bimodal technology and has high molar mass. .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | |
Arkema Group Rilsan® 6733 Nylon 11, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA11/xx,E,18-002Transparent and flexible copolymer for tubes extrusion. Additive free.High flexibility. Very good transparency. High chemical resistance.USP XXIII class VI appro.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 - 91.0 °C | 156 - 196 °F | Average value: 82.2 °C Grade Count:13 |
Overview of materials for Cellulose Acetate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate, Molded". Each property range of values reported is minimum and maximum values of appr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ISO 75 |
Eastman 9921W PET Injection Molded
(discontinued **) Voridian PET 9921W is a copolymer PET. Typical applications include containers for automotive parts, household products, and pharmaceutical and food packaging. Voridian PET thermoplastic polyesters .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | ASTM D648 |
Eastman 9921W PET Injection Molded
(discontinued **) Voridian PET 9921W is a copolymer PET. Typical applications include containers for automotive parts, household products, and pharmaceutical and food packaging. Voridian PET thermoplastic polyesters .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 68.9 - 142 °C | 156 - 288 °F | Average value: 104 °C Grade Count:30 |
Overview of materials for Ethylene Butyl Acrylate This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Butyl Acrylate". Each property range of values reported is minimum and maximum values of approp.. |