Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 270 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	75.0 - 270 °C	167 - 518 °F	Average value: 180 °C Grade Count:10
Overview of materials for Polyphenylene Sulfide (PPS); Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS); Molded". Each property range of values reported is minimum and maximum valu..
Deflection Temperature at 1.8 MPa (264 psi)	105 - 270 °C	221 - 518 °F	Average value: 255 °C Grade Count:23
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%..
Deflection Temperature at 1.8 MPa (264 psi)	220 - 270 °C	428 - 518 °F	Average value: 254 °C Grade Count:15
Overview of materials for Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler". Specific grades with carbon fiberr content be..
Deflection Temperature at 1.8 MPa (264 psi)	235 - 270 °C	455 - 518 °F	Average value: 262 °C Grade Count:17
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Deflection Temperature at 1.8 MPa (264 psi)	260 - 270 °C	500 - 518 °F	Average value: 264 °C Grade Count:20
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Deflection Temperature at 1.8 MPa (264 psi)	260 - 270 °C	500 - 518 °F	Average value: 265 °C Grade Count:11
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Deflection Temperature at 1.8 MPa (264 psi)	249 - 270 °C	480 - 518 °F	Average value: 262 °C Grade Count:18
Overview of materials for Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler". Each property range of values reported is ..
Deflection Temperature at 1.8 MPa (264 psi)	180 - 270 °C	356 - 518 °F	Average value: 220 °C Grade Count:16
Overview of materials for Nylon 66/6, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are incl..