Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Pyrotek Pyrocast ZI Refractory Shapes Aggregate Base: BauxiteApplicationsCrucible bottoms Information provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | Deformation under load - t<sub>a</sub> |
Gouda Vuurvast AK 94 M Dense Refractory Brick Description: This mullite bonded, corundum brick combines a very good thermal shock resistance with a low creep as well as with resistance against a large variety of slags. (after 50 hours at 1650Â.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Gouda Vuurvast AK 94 M Dense Refractory Brick Description: This mullite bonded, corundum brick combines a very good thermal shock resistance with a low creep as well as with resistance against a large variety of slags. (after 50 hours at 1650Â.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Gouda Vuurvast CURAS 90 D Moldable Refractory Material Description: This material is supplied as a dry powder, it has to be mixed with potable water to the necessary consistency. This high refractory ramming material contains several well defined corund.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Gouda Vuurvast CURAS 90 Moldable Refractory Material Description: This high refractory ramming material contains several well defined corundum qualities and only a small quantity of binding agent. Curas 90 has a very good resistance against erosion an.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
BNZ Materials Blazecrete 3200 Dense Castable Blazecrete 3200 is a high alumina castable for service to 3200°F (1778°C). It has good volume stability, extremely high modulus of rupture and crushing strength, and is of high purity for special .. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | Normal oxidizing atmosphere |
BNZ Materials BNZ-32 Insulating Firebrick BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirem.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Ceramabind™ 644-S High Temperature Inorganic Binder A colloidal silica aqueous solution which produces high adhesive strength. Ideal for blending with all types of granular and fibrous ceramics. Excellent resistance to temperature, moisture and mecha.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Ceramabond™ 516 High Temperature Ceramic Adhesive/Paste, Zirconia Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Ceramabond™ 571 High Temperature Ceramic Adhesive/Paste, Magnesium Oxide Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Ceramabond™ 671 High Temperature Ceramic Adhesive/Paste, Alumina Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Ceramabond™ 885 High Temperature Ceramic Adhesive/Paste, Zirconia Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Ceramacast™ 510 High Temperature Potting & Casting Material Alumina Coarse grain castable for producing large hi-temp tooling. |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Pyro-Paint™ 634-ALP High Temperature Refractory Coating This phosphate-bonded, alumina coating system bonds exceptionally well to dense refractory ceramics, providing high abrasion and corrosion resistance for operating temperatures to 3200°F (1760°C) |
|||
Maximum Service Temperature, Air | 1760 °C | 3200 °F | |
Aremco Pyro-Paint™ 634-AL High Temperature Refractory Coating This pure, alumina based compound creates a hard, high temperature resistant coating for refractory fiber boards and shapes, providing exceptional resistance to molten metals and open flames to 3200.. |