Processing Properties | Metric | English | Comments |
---|---|---|---|
Pot Life | 6.0 - 10 min | 6.0 - 10 min | anti-slump |
ACC QSil 430 QSI Quantum Silicones Silicone Potting Material
(discontinued **) Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: 100% solid, quick curing, flame retardant, great adhesion to a variety of substrates. |
|||
Pot Life | 6.0 - 8.0 min | 6.0 - 8.0 min | Time before parts must be mated |
Lord Adhesives 204 Semi-Flexible, Medium Cure, High Viscosity Acrylic Adhesive Lord 200 SeriesLord 200 Series Acrylic Adhesives bond minimally prepared or unprepared surfaces. They offer excellent adhesion to unprepared metals, ceramic magnets and plastics. Viscosities range f.. |
|||
Pot Life | 6.0 - 10 min | 6.0 - 10 min | Time before parts must be mated |
Lord Adhesives 406 Flexible, High Impact and Peel Resistance, Medium Working Time Acrylic Adhesive Lord 400 SeriesLord 400 Series Acrylic Adhesives offer extremely high impact and peel strength. The bond minimally prepared metals and plastics, and achieve high shear strengths. They also provide e.. |
|||
Pot Life | 6.0 - 10 min | 6.0 - 10 min | Time before parts must be mated |
Lord Adhesives 7500C Two-Component, 100% Solids Urethane Adhesive Lord Urethane AdhesivesLord® one- and two-part urethane adhesives provide superior bonds with minimal surface preparation for today's high performance thermosets and thermoplastics. They offe.. |
|||
Pot Life | 6.0 - 8.0 min | 6.0 - 8.0 min | Time before parts must be mated |
Lord Adhesives 7544 Two-Component, Non-Sag, Fast-Cure Urethane Adhesive Lord Urethane AdhesivesLord® one- and two-part urethane adhesives provide superior bonds with minimal surface preparation for today's high performance thermosets and thermoplastics. They offe.. |
|||
Pot Life | 6.0 - 8.0 min | 6.0 - 8.0 min | Time before parts must be mated |
Lord Adhesives 7545C Two-Component, Equal-Mix, Non-Sag Urethane Adhesive Lord Urethane AdhesivesLord® one- and two-part urethane adhesives provide superior bonds with minimal surface preparation for today's high performance thermosets and thermoplastics. They offe.. |
|||
Pot Life | 6.0 min | 6.0 min | |
Taiwan PU Corporation PTMG CPU-167L Polyurethane Casting Elastomer A urethane elastomer that can be cured by reacting with a polyamine or a polyolhardener. The molding process is composed of pre-heating, degassing, maxing with a hardener, pouring into the mold, cu.. |
|||
Pot Life | >= 6.0 min | >= 6.0 min | at ambient temperatures |
Master Bond EP112M Two Component, Medium Viscosity Heat Curing Cycloaliphatic Epoxy Resin Product Description: Master Bond Polymer System EP112M is a solventless, medium viscosity two component cycloaliphatic epoxy resin system which is specifically designed for high performance outdoor .. |
|||
Pot Life | 6.0 - 12 min @Temperature 24.0 °C |
6.0 - 12 min @Temperature 75.2 °F |
1lb mass |
BCC Products BC 4544 Polyester Carvable Wood Filler This polyester resin base compound is easy to use, sets in minutes and can be sanded or carved almost immediately. Acts like wood yet exhibits no grain problems. BC4544 Wood Filler can be carved, sa.. |
|||
Pot Life | 6.0 - 10 min @Temperature 24.0 °C |
6.0 - 10 min @Temperature 75.2 °F |
gel time |
BCC Products BC 4558 Polyester Filler Paste BC4558 is a unique quickset paste designed for aircraft use in making fast repairs to damaged metal surfaces. Also recommended for use in edge filling honeycomb core and foam core composite panels. .. |
|||
Pot Life | 6.0 - 8.0 min @Temperature 24.0 °C |
6.0 - 8.0 min @Temperature 75.2 °F |
gel time |
BCC Products BC 4570 Polyester Hi Heat Filler BC 4570 is a multi-purpose paste designed for making quick repairs to a variety of substrates where service temperature exceeds 200º F (93º C). It is easy to mix and apply, cures in 15-20 minutes .. |
|||
Pot Life | 6.0 - 7.0 min @Temperature 24.0 °C |
6.0 - 7.0 min @Temperature 75.2 °F |
1 lb. mass |
BCC Products METAL-KAST BC 8010 Urethane Casting New BC8010 is a quick setting urethane reproduction plastic system that simulates many of the desirable characteristics of aluminum metal. A highly machineable tooling material that is now easier to.. |