Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 0.0667 min | 0.00111 hour | Steel, handling time |
Permabond 795 Cyanoacrylate, Surface insensitive PERMABOND® 795 is a moderate viscosity, surface insensitive adhesive that will rapidly bond substrates with acidic surfaces such as wood and plated surfaces. Plastics, metals, ceramics and elastome.. |
|||
Cure Time | 0.0667 min | 0.00111 hour | Buna N Rubber, handling time |
Permabond 795 Cyanoacrylate, Surface insensitive PERMABOND® 795 is a moderate viscosity, surface insensitive adhesive that will rapidly bond substrates with acidic surfaces such as wood and plated surfaces. Plastics, metals, ceramics and elastome.. |
|||
Cure Time | 0.0667 min | 0.00111 hour | Phenolic, handling time |
Permabond 795 Cyanoacrylate, Surface insensitive PERMABOND® 795 is a moderate viscosity, surface insensitive adhesive that will rapidly bond substrates with acidic surfaces such as wood and plated surfaces. Plastics, metals, ceramics and elastome.. |
|||
Cure Time | 0.0667 - 0.100 min | 0.00111 - 0.00167 hour | Plastic set time |
Lord Adhesives 7700 Fast Setting, High Viscosity, Impact Resistant. Ethyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLord® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal.. |
|||
Cure Time | 0.0667 - 0.100 min | 0.00111 - 0.00167 hour | Rubber set time |
Lord Adhesives 7700 Fast Setting, High Viscosity, Impact Resistant. Ethyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLord® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal.. |
|||
Cure Time | 0.0667 - 0.0833 min | 0.00111 - 0.00139 hour | Plastic set time |
Lord Adhesives 8400 Fast Setting, Medium Viscosity Ethyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLord® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal.. |
|||
Cure Time | 0.0667 - 0.0833 min | 0.00111 - 0.00139 hour | Plastic set time |
Lord Adhesives 9900 Normal Setting, High Viscosity, Odorless, Non-Frosting Methyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLord® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal.. |
|||
Cure Time | 0.0667 min | 0.00111 hour | Hot tack |
Valley Adhesives EM-220 Low Temperature Application Glue Stick Valley Adhesives EM-220 Low Temperature Application Glue StickBonds many plastics, polyolefins and light weight heat sensitive materials. |
|||
Cure Time | 0.0667 min | 0.00111 hour | 400 W/inch @ 6" |
Tra-Con Tra-Bond F175T One-Part Thixotropic UV Curing Adhesive TRA-BOND F175T is a thixotropic, one part UV curing adhesive designed for bonding metals, ceramics and most rigid polymers. It is an excellent adhesive for fiber optic terminations where fast cure w.. |
|||
Cure Time | 0.0667 min | 0.00111 hour | 400 W/inch @ 6" |
Tra-Con Tra-Bond F175 One-Part UV Curing Adhesive TRA-BOND F175 is a clear, one part UV curing adhesive designed for bonding metals, ceramics and most rigid polymers. It is an excellent adhesive for fiber optic terminations where fast cure with ult.. |
|||
Cure Time | 0.0667 - 0.417 min | 0.00111 - 0.00695 hour | Time to Handling Strength |
3M Scotch-Weld™ PR600 Plastic and Rubber Instant Adhesive 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive is designed to give exceptional performance on difficult-to-bond plastic and rubber substrates. This adhesive may be bonded to like substrates .. |
|||
Cure Time | 0.0667 - 0.417 min | 0.00111 - 0.00695 hour | Time to Handling Strength |
3M Scotch-Weld™ PR600B Plastic and Rubber Instant Adhesive 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive is designed to give exceptional performance on difficult-to-bond plastic and rubber substrates. This adhesive may be bonded to like substrates .. |