Polymer Property : Cure Time = 0.417 min Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	0.250 - 0.417 min	0.00417 - 0.00694 hour	Per 1 mm of wall thickness, injection molding
Hexion Bakelite™ EP 8414 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage (dis Epoxy molding compound, inorganically filled, glass fiber reinforced, highly heat resistant, good electrical even at higher temperatures, very slight post shrinkage, increased media resistance, UL l..
Cure Time	0.250 - 0.417 min	0.00417 - 0.00694 hour	Metal set time
Lord Adhesives 5000 Fast Setting, High Elasticity, Low Viscosity Ethyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLordÂ® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	Metal set time
Lord Adhesives 7000 Medium Setting, Medium Viscosity, Moisture Resistant Methyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLordÂ® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	Plastic set time
Lord Adhesives CA High Viscosity, General Purpose, Non Stringing, Non Migrating Ethyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLordÂ® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATG 115 Phenolic Molding Organic Filler, Compression Molded Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- Black, BrownSoft/medium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic ..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATM 122 Phenolic Molding Organic Filler, Compression Molded Characteristics:Good mouldability Good mechanical strengthGood electrical insulationGood surface finishMedium thermal stabilityColor- black, brownSoft/medium flow Applications: Electric control pane..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATM 123 Phenolic Molding Organic Filler, Compression Molded Characteristics:Glossy surface free of filler marks Surface good & free of flaws Good mouldabilitySurface free of filler marks even after turningGood mechanical strengthColor-black, brownMedium flow..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATM 125 Phenolic Molding Organic Filler, Compression Molded Characteristics:Glossy surface free of filler marks Surface good & free of flaws Good mouldabilitySurface free of filler marks even after turningGood mechanical strengthColor-black, brownSoft/medium..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATM 144 Phenolic Molding Organic Filler, Compression Molded Characteristics:Good mouldability Good mechanical strengthGood electrical insulationGood surface finishMedium thermal stabilityColor- black, brownSoft/medium flow Applications: Electric control pane..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATO 142 Phenolic Molding Organic Filler, Compression Molded Characteristics:Electrical low loss Good mechanical strengthHigh electrical insulationGood mechanical strengthGlossy surfaceLow water absorptionColor-black, brownMedium/hard flow Applications: Elec..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATG 112 Phenolic Molding Organic Filler, Compression Molded Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- Black, BrownSoft/medium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic ..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATG 116 Phenolic Molding Organic and inorganic Filler, Compression Molded Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- BlackMedium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic appliance ha..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	per mm
Amity Thermosets ATO 145 Phenolic Molding Organic Filler, Compression Molded Characteristics:Electrical low loss Good mechanical strengthHigh electrical insulationGood mechanical strengthGlossy surfaceLow water absorptionColor-black, brownMedium flow Applications: Electric ..
Cure Time	0.0667 - 0.417 min	0.00111 - 0.00695 hour	Time to Handling Strength
3M Scotch-Weld™ PR600 Plastic and Rubber Instant Adhesive 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive is designed to give exceptional performance on difficult-to-bond plastic and rubber substrates. This adhesive may be bonded to like substrates ..
Cure Time	0.0667 - 0.417 min	0.00111 - 0.00695 hour	Time to Handling Strength
3M Scotch-Weld™ PR600B Plastic and Rubber Instant Adhesive 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive is designed to give exceptional performance on difficult-to-bond plastic and rubber substrates. This adhesive may be bonded to like substrates ..
Cure Time	0.333 - 0.417 min	0.00556 - 0.00694 hour	Fixture Rate
Dymax Magnet Bonder™ 2010 Adhesive DYMAX® Magnet Bonder™ Adhesives for Higher Performance and Lower CostDymax 2010 Magnet Bonder™ AdhesiveHigh performance; bond plated materials, E-coat Typical Use: D.C. motor magnet to can bond..
Cure Time	0.250 - 0.417 min	0.00417 - 0.00694 hour	Per 1 mm of wall thickness, injection molding
Hexion Bakelite™ EP 8412 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage Epoxy molding compound, inorganically filled, glass fiber reinforced, heat resistant, dimensionally stable, good electrical and mechanical properties, very good chemical resistance, low viscosity, U..