3M Scotch-Weld™ DP100 FR Epoxy Adhesive

Category Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ DP100 FR Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Epoxy Adhesive DP100 FR is a two-part flame retardant (self-extinguishing) version of Scotch-Weld DP100. It meets the UL94 V-O Burn Test requirements and has a work life of 4-8 minutes after mixing. It is ideal for many applications requiring a self-extinguishing structural epoxy adhesive system.Information provided by 3M
Physical Properties Metric English Comments
Brookfield Viscosity 45000 - 90000 cP
45000 - 90000 cP
Base, RVF #7 spindle, 20 rpm
40000 - 120000 cP
40000 - 120000 cP
Accelerator, RVF #7 spindle, 20 rpm
Mechanical Properties Metric English Comments
Hardness, Shore D 87
87
ASTM D2240
Modulus of Elasticity 4.48 GPa
650 ksi
Shear Strength 1.00 MPa
145 psi
Overlap, Polyacrylic
1.38 MPa
200 psi
Overlap, Polycarbonate
1.65 MPa
240 psi
Overlap, PVC
2.90 MPa
420 psi
Overlap, ABS
4.14 MPa
600 psi
Overlap, FRP
7.24 MPa
1050 psi
Overlap, Aluminum-MEK/abrade/MEK
7.58 MPa
1100 psi
Overlap, Cold Rolled Steel-MEK/abrade/MEK
14.5 MPa
2100 psi
Overlap, after tap water 30 days @ 23°C
15.2 MPa
2200 psi
Overlap, Aluminum-Etched
15.2 MPa
2200 psi
Overlap, after 50% RH/RT/30 days
18.6 MPa
2700 psi
Overlap, after salt spray 30 days @ 23°C
8.62 MPa

@Temperature -55.0 °C
1250 psi

@Temperature -67.0 °F
Overlap
15.2 MPa

@Temperature 23.0 °C
2200 psi

@Temperature 73.4 °F
Overlap
5.52 MPa

@Temperature 82.0 °C,
Time 900 sec
800 psi

@Temperature 180 °F,
Time 0.250 hour
Overlap
Peel Strength 0.351 kN/m
2.00 pli
90° T-Peel, Aluminum, etched 2024 T-3; ASTM D1876-61T
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 142 °C
288 °F
Processing Properties Metric English Comments
Cure Time 10.0 - 20.0 min
0.167 - 0.333 hour
Time to Handling Strength
1440 - 2880 min
24.0 - 48.0 hour
Descriptive Properties Value Comments
Appearance Cream