Arkema Group Rilsamid® PA 12 AMNO MED Nylon 12

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer Arkema
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsamid® PA 12 AMNO MED Nylon 12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rilsamid® AMNO MED is a thermoplastic polyamide 12. This grade dedicated to injection offers the highest quality and it is specifically designed to meet the stringent requirements of the medical applications such as minimally invasive devices. Upon request letters regarding USP Class VI compliance can be provided. Designation: PA12, M, 12-010Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
ISO 1183
Water Absorption 0.90 %

@Temperature 23.0 °C,
Time 86400 sec
0.90 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.70 %

@Temperature 20.0 °C
0.70 %

@Temperature 68.0 °F
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Thickness 2.00 mm,
Time 86400 sec
0.0080 in/in

@Thickness 0.0787 in,
Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Thickness 2.00 mm,
Time 86400 sec
0.0080 in/in

@Thickness 0.0787 in,
Time 24.0 hour
Mechanical Properties Metric English Comments
Hardness, Shore D 72
72
After 15 sec, Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 64.0 MPa
9280 psi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Tensile Strength, Yield 38.0 MPa
5510 psi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Elongation at Break <= 250 %
<= 250 %
Conditioned 15 days at 23°C - 50% RH; ISO 527
Elongation at Yield 7.0 %
7.0 %
Conditioned 15 days at 23°C - 50% RH; ISO 527
Tensile Modulus 1.17 GPa
170 ksi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Flexural Modulus 1.20 GPa
174 ksi
Conditioned 15 days at 23°C - 50% RH; ISO 178
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179
0.900 J/cm²

@Temperature 23.0 °C
4.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 180 °C
356 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75
Processing Properties Metric English Comments
Nozzle Temperature 250 °C
482 °F
Recommended
230 - 280 °C
446 - 536 °F
Mold Temperature 40.0 °C
104 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour