Arlon R30370A008 0.008" Uncured Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon R30370A008 0.008" Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Interleave: 0.001" FEP FilmSide 1: Unsupported/Uncured Silicone RubberSubstrate: 0.003" PTFE coated FiberglassThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
Physical Properties Metric English Comments
Thickness 76.2 microns
3.00 mil
Substrate
203 microns
8.00 mil
Rubber
Mechanical Properties Metric English Comments
Hardness, Shore A >= 60
>= 60
Silicone Property
Tensile Strength 5.17 MPa
750 psi
Silicone Property
Elongation at Break 275 %
275 %
Silicone Property
Shear Modulus <= 0.000689 GPa
<= 0.100 ksi
Shear Strength >= 2.76 MPa
>= 400 psi
Lap
Thermal Properties Metric English Comments
Thermal Conductivity 0.320 W/m-K
2.22 BTU-in/hr-ft²-°F
Maximum Service Temperature, Inert 232 °C
450 °F
Minimum Service Temperature, Air -73.3 °C
-100 °F
Electrical Properties Metric English Comments
Dielectric Strength 13.8 kV/mm
350 kV/in
Processing Properties Metric English Comments
Cure Time 15.0 min

@Temperature 121 °C
0.250 hour

@Temperature 250 °F
Recommended Cure Cycle
Shelf Life 3.00 Month
3.00 Month
Descriptive Properties Value Comments
Color Light Blue
Thermal Impedance (°C/W) 0.7
Total Product Weight (oz/yd2) 9