BASF Ultradur® S 4090 G6X High Speed 30% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur® S 4090 G6X High Speed 30% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Low-warpage, easy-flowing injection molding grade with 30 % glass fibers for technical parts, for which dimensional stability is very important, reduction of wall thickness (eg, e/e housings, plug-and-socket connectors.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.600 - 0.900 g/cc
0.0217 - 0.0325 lb/in³
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62
Viscosity Measurement 95
95
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0013 cm/cm
0.0013 in/in
plate with film gate 150x150x3mm<sup>3</sup>
0.0032 cm/cm
0.0032 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.00889 cm/cm
0.00889 in/in
plate with film gate 150x150x3mm<sup>3</sup>
0.0097 cm/cm
0.0097 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
ISO 527-1/-2
Elongation at Break 2.2 %
2.2 %
ISO 527-1/-2
Tensile Modulus 9.50 GPa
1380 ksi
ISO 527-1/-2
Charpy Impact Unnotched 4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.780 J/cm²

@Temperature 23.0 °C
3.71 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 223 °C
433 °F
ISO 11357-1/-2
Maximum Service Temperature, Air 170 °C
338 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
Decomposition Temperature >= 300 °C
>= 572 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+15 ohm-cm
2.00e+15 ohm-cm
IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
IEC 60250
3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0046

@Frequency 100 Hz
0.0046

@Frequency 100 Hz
IEC 60250
0.0202

@Frequency 1.00e+6 Hz
0.0202

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 425 V
425 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection molding/Extrusion
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection molding
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929