BASF Ultramid® 8262G HS BK-102 7/13% Glass/Mineral Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8262G HS BK-102 7/13% Glass/Mineral Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8262G HS BK-102 is a heat stabilized, pigmented black, 20% glass and mineral reinforced PA6 injection molding compound resulting in a balance of engineering properties with excellent dimensional stability, low warp and good resistance to sink mark formation.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Water Absorption 1.3 %
1.3 %
24 hour; ISO Test
7.9 %
7.9 %
ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM Test
Tensile Strength at Break 100 MPa
14500 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 100 MPa
14500 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
3.0 %
3.0 %
0.2 in/min; ASTM Test
Tensile Modulus 5.20 GPa
754 ksi
1mm/min; ISO 527
Flexural Strength 170 MPa
24700 psi
ASTM Test
Flexural Modulus 4.20 GPa
609 ksi
ISO Data
4.60 GPa
667 ksi
ASTM Test
Izod Impact, Notched 0.450 J/cm

@Thickness 3.17 mm
0.843 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Unnotched 4.80 J/cm
8.99 ft-lb/in
ASTM Test
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO Test
3.00 kJ/m²

@Temperature -40.0 °C
1.43 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 211 °C
412 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 163 °C
325 °F
ISO 75
193 °C
379 °F
ASTM Test
Flammability, UL94 HB
HB
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes