BASF Ultramid® Structure B3WG10 LF High-Performance Long-Glass Fiber Reinforced Polyamide

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® Structure B3WG10 LF High-Performance Long-Glass Fiber Reinforced Polyamide.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Mechanical Properties Metric English Comments
Tensile Strength 118 MPa

@Temperature 120 °C
 17100 psi

@Temperature 248 °F
Tensile Modulus 7.335 GPa

@Temperature 120 °C
 1064 ksi

@Temperature 248 °F
Charpy Impact, Notched 1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
3.50 J/cm²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 Conditioned: 15 days, 70°C, 70% humidity
3.70 J/cm²

@Temperature 23.0 °C
 17.6 ft-lb/in²

@Temperature 73.4 °F
Dart Drop, Total Energy 4.50 J

@Temperature -30.0 °C
 3.32 ft-lb

@Temperature -22.0 °F
9.00 J

@Temperature 23.0 °C
 6.64 ft-lb

@Temperature 73.4 °F
Tensile Creep Modulus, 1000 hours 40.0 MPa

@Temperature 120 °C
 5800 psi

@Temperature 248 °F
Descriptive Properties Value Comments
Commercial Status Europe
Continuous Vibration Test Cycles 70 Mpa
R= -1
Creep Elongation 0.4
1 hr @ 40 Mpa, 120°C,
0.43
1 hr @ 40 Mpa, 150°C,
0.5
100 hr @ 40 Mpa, 120°C,
0.5
100 hr @ 40 Mpa, 150°C,
0.54
1000 hr @ 40 Mpa, 120°C,
0.55
1000 hr @ 40 Mpa, 150°C,