Borealis LE6022 Polyethylene Modified Jacketing Compound

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Wire/Cable Grade
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis LE6022 Polyethylene Modified Jacketing Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LE6022 is a black low density copolymer modified polyethylene compound. It is characterized by excellent crack resistance and mechanical properties and low temperature performance in combination with good extrudability. LE6022 contains 2,5% well dispersed furnace black of nominal particle size less than 25 nanometers in order to ensure excellent weathering resistance. Applications: LE6022 is designed for jacketing of communication cables. Specifications: ASTM D1248 Type I, Class C, Category 5, Grade E5, J3, W2-4; BS 6234: Type 03C, TS1; DIN VDE 0207 Type 2YM2; EN 50290-2-24; HD 620 S1, Part 1, table 4B, DMP 17; IEC 60708; IEC 60840, Type ST3; ISO 1872-PE, KCHL, 18-D003; and IEC 60502, Part 2, Type ST3.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
base resin; ISO 1183
0.931 g/cc
0.0336 lb/in³
compound; ISO 1183
Environmental Stress Crack Resistance >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
Igepal 100%; F20; IEC 60811-4-1/B
Melt Flow 0.20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
1s; ISO 868
Tensile Strength at Break >= 15.0 MPa
>= 2180 psi
50mm/min; ISO 527
Elongation at Break >= 600 %
>= 600 %
50mm/min; ISO 527
Flexural Modulus 0.250 GPa
36.3 ksi
ISO 178
Thermal Properties Metric English Comments
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+6 ohm-cm
1.00e+6 ohm-cm
DC; IEC 60093
Dielectric Constant 2.5

@Frequency 1.00e+6 Hz
2.5

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength >= 20.0 kV/mm
>= 508 kV/in
IEC 60243
Dissipation Factor 0.0060

@Frequency 1.00e+6 Hz
0.0060

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Processing Temperature 80.0 - 100 °C
176 - 212 °F
conductor preheating temperature
Melt Temperature 200 - 210 °C
392 - 410 °F