Borealis RF926MO Polypropylene, Transparent Random Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Borealis |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis RF926MO Polypropylene, Transparent Random Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
RF926MO is a specially modified transparent polypropylene random copolymer with high melt flow. This grade is intended for injection stretch blow molding (ISBM). and is designed for high-speed injection molding and contains nucleating and demolding additives. Products molded from this grade exhibit excellent transparency, very good organoleptic properties, high impact strength at ambient temperature, relatively high stiffness, and good demolding and antistatic properties. Applications: bottles for detergents and for the food industry, and jars.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 82 | 82 | ISO 2039-2 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 11 % | 11 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.15 GPa | 167 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75-2 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 5.0 % | <= 5.0 % | Borealis Method |
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 130 °C | <= 266 °F | reheat temperature |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 30.0 - 40.0 °C | 86.0 - 104 °F | |
| Injection Pressure | 0.500 - 2.00 MPa | 72.5 - 290 psi | |
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Velocity | high |