Chevron Phillips Marlex® H516 Polyethylene; HDPE  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips Marlex® H516 Polyethylene; HDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High density polyethylene compound. This high performance PE 100 HDPE compound is tailored for the demanding requirements of pressure pipe applications that require: Excellent long-term hoop strengthSuperb resistance to slow-crack growthExceptional resistance to rapid-crack propagationOutstanding low-temperature toughness Additional information: Yellow version also available.Applications: Typical pipe applications for H516 include: Gas distributionPotable waterIndustrial applicationsInformation provided by PhillipsThis compound meets or exceeds: ASTM D4976 - PE 235ASTM D3350, class 445574C and 445576CNSF Standards 14 and 61 for potable waterPPI designations PE 4710 and PE 100
Physical Properties Metric English Comments
Density 0.961 g/cc
0.0347 lb/in³
ASTM D-1505
Melt Flow 8.0 g/10 min
8.0 g/10 min
HLMI, 190/21.6; ASTM D-1238
Mechanical Properties Metric English Comments
PENT >= 5000 hour
>= 5000 hour
slow crack growth; ASTM F-1473
Tensile Strength, Yield 25.5 MPa
3700 psi
2 in/min, Type IV bar; ASTM D-638
Elongation at Break >= 700 %
>= 700 %
2 in/min, Type IV bar; ASTM D-638
Flexural Modulus 0.965 GPa
140 ksi
2% Secant - 16:1 span:depth, 0.5 in/min; ASTM D-790
Hydrostatic Design Basis 11.0 MPa

@Temperature 23.0 °C
1600 psi

@Temperature 73.4 °F
ASTM D-2837
Descriptive Properties Value Comments
Hydrostatic Design Basis @ 140°F MPa 6.9
ASTM D-2837
Hydrostatic Strength, hour >10000
at 5.0MPa, 80°C; ISO 1167
>400
at 12.4Mpa, 20°C; ISO 1167
>8000
at 5.5MPa, 80°C; ISO 1167
Notched Pipe Test @ 4.6 MPa hour 500
ISO 13479
Rapid Crack Propagation bar >10
S4 crit. pressure, -15°C; ISO 13477
30
Full Scale Test, 0°C; ISO 13478
Required Minimum Strength MPa 10
ISO 9080