Covestro Bayblend® FR3050 PC/ABS Blend

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR3050 PC/ABS Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injection molding• High heat resistant• Improved chemical resistance and stress cracking behaviorAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183-1
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62, 50% RH
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62
Viscosity 480000 cP

@Shear Rate 1000 1/s,
Temperature 260 °C
480000 cP

@Shear Rate 1000 1/s,
Temperature 500 °F
melt viscosity; b.o. ISO 11443-A
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.00 mm
0.0050 - 0.0070 in/in

@Thickness 0.118 in
150x105x3mm; b.o. ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %
>= 50 %
50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO) 55.0 kJ/m²

@Temperature 23.0 °C
26.2 ft-lb/in²

@Temperature 73.4 °F
ISO 180-A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180-U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
37.8 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 68.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
37.8 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 126 °C
259 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 115 °C
239 °F
ISO 75-1,-2
Vicat Softening Point 134 °C

@Load 5.10 kg
273 °F

@Load 11.2 lb
50°C/h; ISO 306
136 °C

@Load 5.10 kg
277 °F

@Load 11.2 lb
120°C/h; ISO 306
Flammability, UL94 V-1

@Thickness 1.00 mm
V-1

@Thickness 0.0394 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94-5V
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94-5V
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
IEC 60093
Surface Resistance 1.00e+17 ohm
1.00e+17 ohm
IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
IEC 60250
3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm

@Thickness 1.00 mm
889 kV/in

@Thickness 0.0394 in
IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz
0.0020

@Frequency 100 Hz
IEC 60250
0.0080

@Frequency 1.00e+6 Hz
0.0080

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 300 V
300 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294