DSM Stanyl® TE250F3 Nylon 46-15% Glass Reinforced (European and Asian Grade) (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Glass Fiber Reinforced
Manufacturer DSM Engineering Plastics
Trade Name Stanyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Stanyl® TE250F3 Nylon 46-15% Glass Reinforced (European and Asian Grade) (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temperatures Excellent resistance to wear and low friction Outstanding flow for easy processing and exceptional design freedomStanyl High Flowgrades that match the best flowing LCPs while maintaining a high level of mechanical propertiesKey Applications: Automotive: Powertrain components, Charge-air coolers, EPS and ETC gears, Motor Sensors, Auto connectors, Chain tensionersE&E: Connectors, Microswitches, Bobbins, Memory modules, Motor components, Industrial, Specialty films and fibers, Consumer appliancesInformation provided by DSM.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.1 %
2.1 %
Humidity Absorption; Sim. to ISO 62
Viscosity Test 145 cm³/g
145 cm³/g
Viscosity Number
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 8.00 GPa
1160 ksi
ISO 527-1/-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Melting Point 295 °C
563 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
ISO 75-1/-2
Vicat Softening Point 290 °C
554 °F
50°C/h 50N; ISO 306
Glass Transition Temp, Tg 75.0 °C
167 °F
Glass Transition Temperature (10°C/min); ISO 11357-1/-2
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL746B
130 °C

@Thickness 0.900 mm
266 °F

@Thickness 0.0354 in
UL746B
UL RTI, Mechanical with Impact 110 °C

@Thickness 0.900 mm
230 °F

@Thickness 0.0354 in
UL746B
110 °C

@Thickness 1.50 mm
230 °F

@Thickness 0.0591 in
UL746B
UL RTI, Mechanical without Impact 110 °C

@Thickness 0.900 mm
230 °F

@Thickness 0.0354 in
UL746B
120 °C

@Thickness 1.50 mm
248 °F

@Thickness 0.0591 in
UL746B
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
IEC 60695-11-10
V-0

@Thickness 0.900 mm
V-0

@Thickness 0.0354 in
IEC 60695-11-10
Glow Wire Test 800 °C

@Thickness 0.750 mm
1470 °F

@Thickness 0.0295 in
Glow Wire Ignition Temperature; IEC 60695-2-13
825 °C

@Thickness 3.00 mm
1520 °F

@Thickness 0.118 in
Glow Wire Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 175 - 249 V
175 - 249 V
PLC 3; UL 746A
Descriptive Properties Value Comments
Flame Retardant Yes
Flame Retarding Agent Yes
Heat stabilized or stable to heat Yes
Injection molding Yes
Lubricants Yes
Platable Yes
Release Agent Yes
With Fillers Yes