DuPont Elvaloy® 3107 AC Ethylene and 7% Butyl Acrylate Copolymer  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Butyl Acrylate
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Elvaloy® 3107 AC Ethylene and 7% Butyl Acrylate Copolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Elvaloy® 3107 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3107 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkage temperature. Elvaloy® 3107 AC is recommended for packaging of deep frozen food, where important properties include heat sealing of the film on high-speed packaging lines.Processing characteristics of Elvaloy® 3107 AC are similar to LDPE and conventional polyethylene extruders are recommended.Information provided by DuPont.
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
ASTM D792 - ISO 1183
Thickness 40.0 microns
1.57 mil
Melt Flow 1.1 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.1 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238 - ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
500 mm/min; ISO 527-3
Film Tensile Strength at Yield, TD 7.00 MPa
1020 psi
500 mm/min; ISO 527-3
Film Elongation at Break, MD 200 %
200 %
500 mm/min; ISO 527-3
Film Elongation at Break, TD 600 %
600 %
500 mm/min; ISO 527-3
Coefficient of Friction, Dynamic 0.45
0.45
MD; ISO 8295
Elmendorf Tear Strength, MD 0.0250 g/micron
0.635 g/mil
ISO 6383/2
Elmendorf Tear Strength, TD 0.0250 g/micron
0.635 g/mil
ISO 6383/2
Dart Drop 7.50 g/micron
191 g/mil
ISO 7765/1A
Film Tensile Strength at Break, MD 24.0 MPa
3480 psi
500 mm/min; ISO 527-3
Film Tensile Strength at Break, TD 18.0 MPa
2610 psi
500 mm/min; ISO 527-3
Optical Properties Metric English Comments
Haze 16 %
16 %
ASTM D1003
Gloss 60 %
60 %
ASTM D2457
Processing Properties Metric English Comments
Rear Barrel Temperature 150 °C
302 °F
Extrusion lamination and extrusion coating
150 °C
302 °F
Cast film
150 °C
302 °F
Blown film
Middle Barrel Temperature 160 °C
320 °F
Blown film
210 °C
410 °F
Cast film
220 °C
428 °F
Extrusion lamination
Front Barrel Temperature 170 °C
338 °F
Blown film
250 °C
482 °F
Cast film
290 °C
554 °F
Extrusion lamination
Adapter Temperature 180 °C
356 °F
Blown film
250 °C
482 °F
Cast Film
290 °C
554 °F
Extrusion lamination
Die Temperature 180 °C
356 °F
Blown film
250 °C
482 °F
Cast film
290 °C
554 °F
Extrusion lamination
Blow-up Ratio (BUR) 2.0
2.0
for 40 micron film
Descriptive Properties Value Comments
BA-Content 7 wt.%
DuPont Method