DuPont Performance Polymers Hytrel® HTR8223 BK320 TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR8223 BK320 TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hytrel® HTR8223 BK320 is designed for blow molding or processing techniques requiring high melt viscosity. It has nominal hardness of 42D, is pigmented black with fine particle size carbon black, and contains a general purpose stabilizer.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
Immersion 24h; ISO 62
0.60 %

@Temperature 23.0 °C,
Time 86400 sec
0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Melt Flow 0.60 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.60 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
2.3 g/10 min

@Load 5.00 kg,
Temperature 230 °C
2.3 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D <= 42
<= 42
ISO 868
<= 45
<= 45
ASTM D2240
38

@Time 15.0 sec
38

@Time 0.00417 hour
ISO 868
Tensile Strength at Break 27.0 MPa

@Temperature 23.0 °C
3920 psi

@Temperature 73.4 °F
ISO 527 (1BA bar)
Tensile Stress 3.50 MPa

@Strain 5.00 %,
Temperature 23.0 °C
508 psi

@Strain 5.00 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
5.50 MPa

@Strain 10.0 %,
Temperature 23.0 °C
798 psi

@Strain 10.0 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
6.80 MPa

@Strain 50.0 %,
Temperature 23.0 °C
986 psi

@Strain 50.0 %,
Temperature 73.4 °F
ISO 527 (1BA bar)
Elongation at Break >= 300 %

@Temperature 23.0 °C
>= 300 %

@Temperature 73.4 °F
50mm/min; ISO 527 (1BA bar)
450 %

@Temperature 23.0 °C
450 %

@Temperature 73.4 °F
ISO 527 (1BA bar)
Tensile Modulus 0.0740 GPa

@Temperature 23.0 °C
10.7 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 0.0440 GPa

@Temperature 100 °C
6.38 ksi

@Temperature 212 °F
ISO 178
0.0790 GPa

@Temperature 23.0 °C
11.5 ksi

@Temperature 73.4 °F
ISO 178
0.210 GPa

@Temperature -40.0 °C
30.5 ksi

@Temperature -40.0 °F
ISO 178
Izod Impact, Notched (ISO) NB

@Temperature -50.0 °C
NB

@Temperature -58.0 °F
ISO 180/1A
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact, Notched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 195 °C
383 °F
10°C/min; ISO 11357-1/-3
Brittleness Temperature -100 °C
-148 °F
ISO 974
Processing Properties Metric English Comments
Melt Temperature 225 °C
437 °F
Optimum; Injection Molding
Mold Temperature 45.0 °C
113 °F
optimum; Injection Molding
40.0 - 50.0 °C
104 - 122 °F
Injection Molding
Drying Temperature 110 °C
230 °F
Blow Molding
110 °C
230 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Blow Molding
3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.020 %
<= 0.020 %
Blow Molding
<= 0.020 %
<= 0.020 %
Injection Molding
Descriptive Properties Value Comments
Appearance Black Color
Extrudable - Blown Film Yes
Extrudable - Cast Film Yes
Extrudable - Coating Yes
Extrudable - Filament Yes
Extrudable - Hose Yes
Extrudable - Sheet Yes
Extrudable - Tubing Yes
Extrudable - Wire and Cable Yes
Extrusion Blow Moldable Yes
Forms Pellets
Generic TPC-ET
Heat Stabilized Yes
Material Status Preliminary Data
Melt Castable Yes
Part Marking Code >TPC-ET<
ISO 11469
Polymer Family TPC-ET
Polymer Type TPC-ET
Processing Method Blow Molding
Product Category Blow Moldable Resins
Region Available - Global Yes
Resin Identification TPC-ET
ISO 1043
RoHS Compliance Contact Manufacturer