DuPont Performance Polymers Sorona® 3301V NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)&

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Sorona® 3301V NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)&.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sorona® 3301V NC010 is an unreinforced polytrimethylene terephthalate resin containing 35% renewably sourced ingredients by weight developed for applications requiring high surface gloss in a broad range of conditions.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.013 cm/cm

@Thickness 2.00 mm
 0.013 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 2.00 mm
 0.014 in/in

@Thickness 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa

@Temperature 23.0 °C
 8700 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 15 %

@Temperature 23.0 °C
 15 %

@Temperature 73.4 °F
 nominal; ISO 527
15 %

@Temperature 23.0 °C
 15 %

@Temperature 73.4 °F
 50mm/min; ISO 527
Elongation at Yield 5.5 %

@Temperature 23.0 °C
 5.5 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 2.40 GPa

@Temperature 23.0 °C
 348 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Modulus 2.40 GPa

@Temperature 23.0 °C
 348 ksi

@Temperature 73.4 °F
 ISO 178
Izod Impact, Notched (ISO) 4.50 kJ/m²

@Temperature 23.0 °C
 2.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 228 °C
442 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 125 °C
257 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 IEC 60695-11-10
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 UL94
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL94
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 UL94
Glow Wire Test 675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 IEC 60695-2-12
675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 Ignition; IEC 60695-2-13
700 °C

@Thickness 0.950 mm
 1290 °F

@Thickness 0.0374 in
 Ignition; IEC 60695-2-13
725 °C

@Thickness 0.950 mm
 1340 °F

@Thickness 0.0374 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V

@Temperature 23.0 °C
 600 V

@Temperature 73.4 °F
 IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Optimum
250 - 270 °C
482 - 518 °F
Mold Temperature 80.0 - 110 °C
176 - 230 °F
100 °C
212 °F
optimum
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Appearance Natural Color
Forms Pellets
Generic Polytrimethylene Terephthalate (PTT)
Material Status Current
Part Marking Code >PTT<
ISO 11469
Processing Method Injection Molding
Product Category Renewably Sourced Resins
Unreinforced Resins
Region Available - Global Yes
Resin Identification PTT
ISO 1043
RoHS Compliance Contact Manufacturer